3D printed polyurethane honeycombs for repeated tailored energy absorption

Fused filament fabrication (FFF) 3D printing of thermoplastic polyurethanes (TPUs) offers a unique capability to manufacture tailorable, flexible cellular structures which can be designed and optimised for specific energy absorbing applications. This paper describes the first application of this methodology in the creation and experimental analysis of 3D printed cellular structures, which are capable of undergoing repeated compressions to densification without failure. A parametric study has been undertaken, capturing the energy absorbing capability of hexagonal arrays manufactured from two types of TPU, with relative densities 0.18–0.49. Arrays were subject to compressions at strain rates 0.03–0.3 s− 1 and were capable of absorbing energies over the range of 0.01–0.34 J/cm3, before recovering elastically. Critically, samples attained a maximum energy absorbing ‘efficiency’ of 0.36, which is comparable to that of traditional expanded closed cell polyurethane foams. The energy absorption behaviour of all structures was found to be dependent on strain rate and cell orientation with respect to the compression direction. This study shows the clear potential of FFF 3D printing for the creation of a new breed of cellular architectures, which are not constrained by existing manufacturing principles, offering the designer the capability to create resilient architectures specifically tailored to operational applications and environmental conditions.

[1]  Gi Dae Kim,et al.  A benchmark study on rapid prototyping processes and machines: Quantitative comparisons of mechanical properties, accuracy, roughness, speed, and material cost , 2008 .

[2]  Shiwei Zhou,et al.  Simple cubic three‐dimensional auxetic metamaterials , 2014 .

[3]  M. Ashby,et al.  Cellular solids: Structure & properties , 1988 .

[4]  Arezki Boudaoud,et al.  Optimal fractal-like hierarchical honeycombs. , 2014, Physical review letters.

[5]  J. Papadopoulos,et al.  Hierarchical honeycombs with tailorable properties , 2012 .

[6]  S. D. Papka,et al.  In-plane compressive response and crushing of honeycomb , 1994 .

[7]  Joseph Miltz,et al.  Energy absorption characteristics of polymeric foams used as cushioning materials , 1990 .

[8]  S. D. Papka,et al.  Biaxial crushing of honeycombs: - Part 1: Experiments , 1999 .

[9]  G. Belingardi,et al.  Characterization of polymeric structural foams under compressive impact loading by means of energy-absorption diagram , 2001 .

[10]  R. Hague,et al.  The design of impact absorbing structures for additive manufacture , 2012 .

[11]  Ben Wang,et al.  Designable dual-material auxetic metamaterials using three-dimensional printing , 2015 .

[12]  Stelios Kyriakides,et al.  In-plane biaxial crushing of honeycombs—: Part II: Analysis , 1999 .

[13]  M. Ashby,et al.  The mechanics of three-dimensional cellular materials , 1982, Proceedings of the Royal Society of London. A. Mathematical and Physical Sciences.

[14]  R. Hague,et al.  An investigation into reinforced and functionally graded lattice structures , 2017 .