Experimental and numerical study of the fatigue behaviour of composite patch reinforced cracked steel plates

Abstract One-side, low cost carbon/epoxy patches were laminated on large scale specimens, which were tested and subsequently modelled with the finite element method. An R  = −1 cyclic loading was applied and patch strains and crack propagation rate were monitored. The experimental results were very encouraging, demonstrating that patches can effectively slow down the crack growth and extend the specimens’ life by a factor of up to 2, despite their relatively low stiffness ratio. Based on some simplified assumptions, FE modelling proved adequate in accurately predicting the crack propagation rate.

[1]  Alain Nussbaumer,et al.  Analysis of cracked steel members reinforced by pre-stress composite patch , 2003 .

[2]  A. Baker.  Bonded composite repair of fatigue-cracked primary aircraft structure , 1999 .

[3]  Wing Kong Chiu,et al.  Composite repairs to rib stiffened panels , 1999 .

[4]  Carlo Poggi,et al.  Fatigue performance of tensile steel members strengthened with CFRP plates , 2009 .

[5]  Dae-Cheol Seo,et al.  Fatigue crack growth behavior of cracked aluminum plate repaired with composite patch , 2002 .

[6]  R.M.V. Pidaparti,et al.  Static characteristics and fatigue behavior of composite-repaired aluminum plates , 2002 .

[7]  Shyan Bob Shen,et al.  Fatigue analysis of cracked thick aluminum plate bonded with composite patches , 2004 .

[8]  Jung-Ju Lee,et al.  Successive 3D FE analysis technique for characterization of fatigue crack growth behavior in composite-repaired aluminum plate , 2004 .

[9]  Carlo Poggi,et al.  Strengthening of tensile steel members and bolted joints using adhesively bonded CFRP plates , 2006 .

[10]  P. Colombi,et al.  Repair of riveted bridge members damaged by fatigue using CFRP materials , 2000 .

[12]  Carlo Poggi,et al.  Prediction of debonding strength of tensile steel/CFRP joints using fracture mechanics and stress based criteria , 2009 .

[13]  Ivan Grabovac,et al.  Bonded composite solution to ship reinforcement , 2003 .

[14]  F. Livingstone,et al.  Oil platforms, destroyers and frigates—case studies of QinetiQ's marine composite patch repairs , 2005 .

[15]  A. Tounsi,et al.  The effect of a bonded hygrothermal aged composite patch on the stress intensity factor for repairing cracked metallic structures , 2003 .

[16]  Navdeep Singh,et al.  Design, analysis and performance of adhesively bonded composite patch repair of cracked aluminum aircraft panels , 2005 .

[17]  M. Belhouari,et al.  Computation of the stress intensity factors for repaired cracks with bonded composite patch in mode I and mixed mode , 2002 .

[18]  D. Ouinas,et al.  FE analysis of the behaviour of octagonal bonded composite repair in aircraft structures , 2008 .

[19]  Dennis Roach,et al.  Validation of bonded composite doubler technology through application oriented structural testing , 1996 .

[20]  D. Ouinas,et al.  Numerical analysis of the performances of the bonded composite patch for reducing stress concentration and repairing cracks at notch , 2003 .

[21]  Alain Nussbaumer,et al.  Crack repair and fatigue life extension of riveted bridge members using composite materials , 2000 .

[22]  Turaga V.R.S. Umamaheswar,et al.  Modelling of a patch repair to a thin cracked sheet , 1999 .

[23]  M. Grédiac,et al.  On the fatigue response of aluminium specimens reinforced with carbon–epoxy patches , 2008 .

[24]  A. Baker,et al.  Bonded repair of aircraft structures , 1988 .

[25]  M.F.S.F. de Moura,et al.  Using a cohesive damage model to predict the tensile behaviour of CFRP single-strap repairs , 2008 .

[26]  D. Ouinas,et al.  4027 - COMPARISON OF DOUBLE AND SINGLE BONDED REPAIRS TO SYMMETRIC COMPOSITE STRUCTURES: A NUMERICAL ANALYSIS , 2004 .