Transparent Nanometric Cubic and Tetragonal Zirconia Obtained by High‐Pressure Pulsed Electric Current Sintering

Transparent samples of cubic (8 mol % yttria) and tetragonal (3 mol % yttria) zirconia were prepared from nanometric powders by the pulsed electric current sintering process. The crystallite size of the resulting dense samples was about 50 nm in both cases. The consolidation pressure had a positive effect on the occurrence of transparency for both modifications. Transmittance in the near infrared for 1 mm thick samples is above the 60 % for the cubic (8 %YSZ) and above 50 % for the tetragonal (3 % YSZ) zirconia, representing between 70 and 80 % of the theoretical values of the two modifications. Samples had a yellowish-brown coloration which was attributed to the presence of color centers. Annealing in oxygen improved transmittance initially, but prolonged annealing resulted in translucent samples. The role of porosity in transmittance is analyzed.

[1]  M. Omori.  Sintering, consolidation, reaction and crystal growth by the spark plasma system (SPS) , 2000 .

[2]  M. Frey,et al.  Bulk glasses and ultrahard nanoceramics based on alumina and rare-earth oxides , 2004, Nature.

[3]  Christos Argirusis,et al.  Oxygen diffusion in yttria stabilised zirconia?experimental results and molecular dynamics calculationsPresented at the 78th International Bunsen Discussion Meeting on , 2003 .

[4]  G. Partridge.  Inorganic materials IV. Transparent ceramics and glass‐ceramics , 1990 .

[5]  Gary Gilde,et al.  Transparent armor materials: Needs and requirements , 2002 .

[6]  C. Greskovich,et al.  Conversion of Polycrystalline Al2O3 into Single‐Crystal Sapphire by Abnormal Grain Growth , 2004 .

[7]  Chen,et al.  Intrinsic electron and hole defects in stabilized zirconia single crystals. , 1990, Physical review. B, Condensed matter.

[8]  Metal Halide Lamps with Ceramic Envelopes: A Breakthrough in Color Control , 1997 .

[9]  Rolf Apetz,et al.  Transparent Alumina: A Light‐Scattering Model , 2003 .

[10]  Nagle,et al.  Color-center-induced band-gap shift in yttria-stabilized zirconia. , 1989, Physical review. B, Condensed matter.

[11]  Jiangxu Li,et al.  Fabrication of Cr4+,Nd3+:YAG transparent ceramics for self-Q-switched laser , 2006 .

[12]  Z. A. Munir,et al.  Enhanced low-temperature protonic conductivity in fully dense nanometric cubic zirconia , 2006 .

[13]  M. Tokita.  Trends in Advanced SPS Spark Plasma Sintering Systems and Technology , 1993 .

[14]  Z. A. Munir,et al.  Fast low-temperature consolidation of bulk nanometric ceramic materials , 2006 .

[15]  B. Savoini,et al.  THERMOCHEMICAL REDUCTION OF YTTRIA-STABILIZED-ZIRCONIA CRYSTALS : OPTICAL AND ELECTRON MICROSCOPY , 1998 .

[16]  Z. Kam,et al.  Absorption and Scattering of Light by Small Particles , 1998 .

[17]  M. Pham-thi,et al.  Transparent polycrystalline neodymium doped YAG: synthesis parameters, laser efficiency , 2003 .

[18]  S. Dub,et al.  Vickers and knoop indentation behaviour of cubic and partially stabilized zirconia crystals , 1995 .

[19]  D. L. Wood,et al.  Refractive index of cubic zirconia stabilized with yttria. , 1982, Applied optics.

[20]  Zhe Zhao,et al.  Formation of tough interlocking microstructures in silicon nitride ceramics by dynamic ripening , 2002, Nature.

[21]  M. Nygren,et al.  Transparent nanocrystalline MgO by rapid and low-temperature spark plasma sintering , 2004 .

[22]  Gary Gilde,et al.  An investigation of the transmission properties and ballistic performance of hot pressed spinel , 2002 .

[23]  N. Browning,et al.  Segregation effects at grain boundaries in fluorite-structured ceramics , 2002 .

[24]  E. Wachsman,et al.  Spectroscopic investigation of oxygen vacancies in solid oxide electrolytes , 1990 .

[25]  H. Hahn,et al.  Sintering Behavior of Nanocrystalline Zirconia Prepared by Chemical Vapor Synthesis , 2004 .

[26]  J. S. Smith,et al.  Cubic Phase Stabilization of Translucent Yttria‐Zirconia at Very Low Temperatures , 1967 .

[27]  G. Spinolo,et al.  Spark plasma sintering and characterization of bulk nanostructured fully stabilized zirconia: Part II. Characterization studies , 2004 .

[28]  U. Herr,et al.  Physics of Nanocrystalline Luminescent Ceramics , 2003 .

[29]  R. Raj,et al.  Grain‐Growth Transition During Sintering of Colloidally Prepared Alumina Powder Compacts , 1988 .

[30]  D. A. Wright,et al.  Optical absorption in current-blackened yttria-stabilized zirconia , 1973 .

[31]  R Ruud Metselaar,et al.  Light scattering by pores in polycrystalline materials: Transmission properties of alumina , 1974 .

[32]  K. Tsukuma.  Transparent titania-yttria-zirconia ceramics , 1986 .

[33]  K. Kakegawa,et al.  Spark Plasma Sintering of Transparent PbZrO3-PbTiO3-Pb(Zn1/3Nb2/3)O3 Ceramics , 2002 .