Hydrogen passivation of ultra-thin low-temperature polycrystalline silicon films for electronic applications

Abstract We have investigated the influence of hydrogen passivation on the electronic properties of ultra-thin polycrystalline silicon layers prepared by the aluminum-induced layer exchange process. Hall effect measurements reveal high hole carrier concentrations in the as-grown poly-Si layers up to several times 10 19  cm −3 . We find a drastic increase of the resistivity after hydrogenation for very thin samples, which is attributed to a combination of two effects: (1) the reduction of free holes due to acceptor passivation and (2) compensation of free holes remaining after H-passivation by interface trap states. Temperature-dependent measurements show that the activation energy of the dark conductivity increases strongly after the hydrogenation process. The origin of the compensation was investigated by spin-dependent transport measurements. In addition, the potential of the passivated poly-Si layers for electronic applications was studied. We have demonstrated a normally ON back-gate depletion mode transistor with a two mask process, which exhibits a field-effect mobility of 21 cm 2 /Vs for holes in the 20 nm thin channel layer.

[1]  Stavola,et al.  Vibrational spectroscopy of acceptor-hydrogen complexes in silicon: Evidence for low-frequency excitations. , 1988, Physical review. B, Condensed matter.

[2]  M. Stutzmann,et al.  Spin-dependent processes in amorphous and microcrystalline silicon: a survey , 2000 .

[3]  J. Seto.  The electrical properties of polycrystalline silicon films , 1975 .

[4]  D. Biegelsen,et al.  Deuterium passivation of grain‐boundary dangling bonds in silicon thin films , 1982 .

[5]  Martin Stutzmann,et al.  Structural and electronic properties of ultrathin polycrystalline Si layers on glass prepared by aluminum-induced layer exchange , 2007 .

[6]  M. Stutzmann,et al.  Thin polycrystalline SiGe films by aluminium‐induced layer exchange , 2004 .

[7]  H. Kwok,et al.  Performance of thin-film transistors with ultrathin Ni-MILC polycrystalline silicon channel layers , 1999, IEEE Electron Device Letters.

[8]  Jacques I. Pankove,et al.  Neutralization of acceptors in silicon by atomic hydrogen , 1984 .

[9]  M. Stutzmann,et al.  Aluminum-induced crystallization of amorphous silicon–germanium thin films , 2004 .

[10]  Ishii,et al.  Origin of the ESR signal with g=2.0055 in amorphous silicon. , 1990, Physical review. B, Condensed matter.

[11]  Akito Hara,et al.  High-Performance Polycrystalline Silicon Thin Film Transistors on Non-Alkali Glass Produced Using Continuous Wave Laser Lateral Crystallization , 2002 .

[12]  Takashi Noguchi,et al.  Low Temperature Poly-Si Thin Film Transistor on Plastic Substrates , 2004, IEICE Trans. Electron..

[13]  F. Trumbore,et al.  Solid solubilities of impurity elements in germanium and silicon , 1960 .

[14]  Alistair B. Sproul,et al.  Aluminum-induced crystallization of amorphous silicon on glass substrates above and below the eutectic temperature , 1998 .

[15]  Stutzmann,et al.  Boron-hydrogen complexes in crystalline silicon. , 1991, Physical review. B, Condensed matter.

[16]  Shuichi Uchikoga,et al.  Low temperature poly-Si TFT-LCD by excimer laser anneal , 2001 .

[17]  Bruce E. Deal,et al.  ESR centers, interface states, and oxide fixed charge in thermally oxidized silicon wafers , 1979 .

[18]  J. Pankove,et al.  Neutralization of Shallow Acceptor Levels in Silicon by Atomic Hydrogen , 1983 .

[19]  H. Dersch,et al.  Recombination processes in a-Si:H: Spin-dependent photoconductivity , 1983 .