The structure of fast-reactor irradiated solution-treated AISI type 316 steel
暂无分享,去创建一个
[1] J. Hudson. Void formation in solution-treated aisi 316 and 321 stainless steels under 46.5 mev ni6+ irradiation , 1976 .
[2] T. Williams,et al. Void-swelling in solution-treated FV548 steel irradiated in a high-voltage electron microscope , 1976 .
[3] T. Williams,et al. Vacancy cluster damage in type 316 stainless steel irradiated with Cr+ ions , 1975 .
[4] N. Yoshida,et al. Point Defect Clusters in Electron-Irradiated Gold , 1973 .
[5] A. M. Turkalo,et al. Nickel-ion bombardment of annealed and cold-worked type 316 stainless steel , 1973 .
[6] H. Brager,et al. Defect development in neutron irradiated type 316 stainless steel , 1973 .
[7] R. Bullough,et al. The rate theory of swelling due to void growth in irradiated metals , 1972 .
[8] E. E. Bloom,et al. RADIATION DAMAGE IN ANNEALED TYPE 304 STAINLESS STEEL. , 1972 .
[9] A. Rowcliffe,et al. The geometry of secondary defects formed on quench-ageing a phosphorous containing stainless steel , 1971 .
[10] K. C. Russell. Nucleation of voids in irradiated metals , 1971 .
[11] L. Singhal,et al. The nucleation and growth of widmannstätten m23c6 precipitation in an austenitic stainless steel , 1968 .
[12] G. Schoeck. Correlation between Dislocation Length and Density , 1962 .
[13] R. Burge,et al. The analytical representation of atomic scattering amplitudes for electrons , 1962 .