Influence of NH3/Ar plasma irradiation on physical and photocatalytic properties of TiO2 nanopowder

Abstract NH3(10%)/Ar plasmas were generated at different gas pressures in a mechanical milling chamber, and were uniformly irradiated on an anatase TiO2 powder with 300 m2/g of which corresponding diameter was 7 nm. Crystal structures of the plasma irradiated powders were the same as that of the raw powder, regardless of the gas pressure. On the other hand, the optical property of the resultant powders was varied with regard to the gas pressure. When plasma generated and irradiated at 300 Pa, the powder had the specific surface area (SSA) of 283 m2/g and noticeable absorption in vis light range was observed. In addition, the powder showed an improvement of the photocatalytic oxidation activity of CH3CHO under vis light. These results indicated that the present plasma treatment is capable of modifying TiO2 nanopowder for improving photoactivity without large SSA reduction, which is often seen in the modification with annealing.

[1]  G. Djéga-Mariadassou,et al.  Preparation and characterization of titanium oxynitrides with high specific surface areas , 1991 .

[2]  T Ihara,et al.  Visible-light-active titanium oxide photocatalyst realized by an oxygen-deficient structure and by nitrogen doping , 2003 .

[3]  R. Asahi,et al.  Visible-Light Photocatalysis in Nitrogen-Doped Titanium Oxides , 2001, Science.

[4]  D. Wexler,et al.  Mechanical milling assisted by electrical discharge , 2002, Nature.

[5]  Yuka Watanabe,et al.  Nitrogen-Concentration Dependence on Photocatalytic Activity of TiO2-xNx Powders , 2003 .

[6]  F. Saito,et al.  Preparation of Visible Light-Activated Titania Photocatalyst by Mechanochemical Method , 2003 .

[7]  J. Weber,et al.  Effect of alkaline-doped TiO2 on photocatalytic efficiency , 2004 .

[8]  G. Neudeck,et al.  Effect of NH3 plasma treatment of gate nitride on the performance of amorphous silicon thin‐film transistors , 1990 .

[9]  M. Anpo,et al.  Design and development of titanium oxide photocatalysts operating under visible and UV light irradiation.: The applications of metal ion-implantation techniques to semiconducting TiO2 and Ti/zeolite catalysts , 2002 .

[10]  R. Asahi,et al.  Band-Gap Narrowing of Titanium Dioxide by Nitrogen Doping , 2001 .

[11]  Koji Takeuchi,et al.  Role of oxygen vacancy in the plasma-treated TiO2 photocatalyst with visible light activity for NO removal , 2000 .

[12]  K. Hashimoto,et al.  Visible-light induced hydrophilicity on nitrogen-substituted titanium dioxide films. , 2003, Chemical communications.