A numerical analysis on the interaction of twin coplanar flaws

In several practical situations, structural components present more than one crack. Such multiple cracks should be considered simultaneously since the interaction phenomenon could produce higher stress-intensity factor (SIF) values with respect to the case of a single crack. In the present paper, the influence of two identical coplanar semi-elliptical surface flaws in a plate with finite width and thickness under various stress distributions perpendicular to the crack faces is numerically analysed. Then the results for such elementary stresses are used to obtain the SIFs for real load cases. Due to the interaction effect, the SIF distribution along the crack front is asymmetric and dependent on the distance δ between the two surface cracks. The distance of non-interaction is evaluated as a function of the crack shape and the crack depth.

[1]  Andrea Carpinteri,et al.  External surface cracks in shells under cyclic internal pressure , 2000 .

[2]  Andrea Carpinteri,et al.  Handbook of fatigue crack propagation in metallic structures , 1994 .

[3]  Andrea Carpinteri.  Interaction of Coplanar Surface Flaws under Tension , 1994 .

[4]  James C. Newman,et al.  Stress-intensity factors for a wide range of semi-elliptical surface cracks in finite-thickness plates , 1979 .

[5]  L. J. Chockie.  The 1974 Edition of Section XI, Rules for Inservice Inspection of Nuclear Power Plant Components , 1975 .

[6]  S. Nemat-Nasser,et al.  Growth and stability of interacting surface flaws of arbitrary shape , 1983 .

[7]  M. Bergman,et al.  STRESS INTENSITY FACTORS FOR CIRCUMFERENTIAL SURFACE CRACKS IN PIPES , 1995 .

[8]  Andrea Carpinteri,et al.  Circumferential surface flaws in pipes under cyclic axial loading , 1998 .

[9]  Shinobu Yoshimura,et al.  Automated System for Analyzing Stress Intensity Factors of Three-Dimensional Cracks: Its Application to Analyses of Two Dissimilar Semi-Elliptical Surface Cracks in Plate , 1997 .

[10]  X. B. Lin,et al.  Fatigue growth analysis of interacting and coalescing surface defects , 1997 .

[11]  Wole Soboyejo,et al.  Fatigue crack propagation of coplanar semi-elliptical cracks in pure bending , 1990 .

[12]  V. V. Panasyuk,et al.  Advances in Fracture Resistance and Structural Integrity , 1994 .

[13]  Dietrich Munz,et al.  Fatigue Crack Propagation in cylindrical bars , 1986 .

[14]  Sia Nemat-Nasser,et al.  Interacting dissimilar semi-elliptical surface flaws under tension and bending , 1982 .