The effect of filler concentration on the electrical, thermal, and mechanical properties of carbon particle and carbon fiber-reinforced poly(styrene-co-acrylonitrile) composites

Composite materials of poly (styrene-co-acrylonitrile) (luran) matrix with carbon fibers (CF)/carbon particles (CP) were prepared and their properties were evaluated. The mechanical and thermal properties of these composites were studied by dynamic mechanical analysis (DMA) and differential scanning calorimetry (DSC). Although, by increasing the filler concentration no significant difference was found in melting and crystallization temperatures of the luran. The storage and tensile modulus of the composites increased linearly with filler concentration up to 40 wt % that was approximately three times higher than that of the virgin luran. There is a shift in glass transition temperature of the composite with increasing the filler concentration and the damping peak became flatter that indicated the effectiveness of the filler–matrix interaction. The volume resistivity and thermal conductivity (TC) of the composites were also measured. At a given carbon filler content the CF–Luran composites have much less volume resistivity as compared to CP–Luran composites. The decreased percolation threshold and volume resistivity in case of CF–Luran composites indicated that conductive paths existed in the composites. The conductive pathways were probably formed through interconnection of the carbon fillers. The volume resistivity was also decreased as a function of temperature. The thermal conductivity was increased linearly as a function of temperature with increasing filler concentration up to 40% of CF and CP. This increase was more profound in case of CF–Luran as compared to CP–Luran composites. This was owing to greater thermal networks of fibers as compared to particles. POLYM. COMPOS., 28:186–197, 2007. © 2007 Society of Plastics Engineers

[1]  A. Amash,et al.  Thermal and dynamic mechanical investigations on fiber-reinforced polypropylene composites , 1997 .

[2]  A. Dasgupta,et al.  Orthotropic Thermal Conductivity of Plain-Weave Fabric Composites Using a Homogenization Technique , 1992 .

[3]  J. Woods,et al.  I-V characteristics of carbon black-loaded crystalline polyethylene , 1993 .

[4]  J. Margolis.  Conductive polymers and plastics , 1989 .

[5]  M. Narkis,et al.  New injection moldable electrostatic dissipative (ESD) composites based on very low carbon black loadings , 1999 .

[6]  N. Tsubokawa,et al.  A novel gas sensor from polymer‐grafted carbon black: responsiveness of electric resistance of conducting composite from LDPE and PE‐b‐PEO‐grafted carbon black in various vapors , 2000 .

[7]  Zachariah Oommen,et al.  Dynamic mechanical analysis of banana fiber reinforced polyester composites , 2003 .

[8]  A. Márquez,et al.  Conductivity variation induced by solvent swelling of an elastomer–carbon black–graphite composite , 1997 .

[9]  Lionel Flandin,et al.  Effect of strain on the properties of an ethylene–octene elastomer with conductive carbon fillers , 2000 .

[10]  S. M. Aharoni,et al.  Electrical Resistivity of a Composite of Conducting Particles in an Insulating Matrix , 1972 .

[11]  K. Miyasaka,et al.  Electrical conductivity of carbon-polymer composites as a function of carbon content , 1982 .

[12]  Sabu Thomas,et al.  Dynamic mechanical properties of short sisal fibre reinforced polypropylene composites , 2003 .

[13]  Tae Jin Kang,et al.  Thermal and ablative properties of low temperature carbon fiber–phenol formaldehyde resin composites , 2002 .

[14]  S. Houshyar,et al.  The effect of fiber concentration on mechanical and thermal properties of fiber-reinforced polypropylene composites , 2005 .

[15]  Marco-A. De Paoli,et al.  Conductive polymer blends: Preparation, properties and applications , 2002 .

[16]  M. Narkis,et al.  Resistivity behavior of filled electrically conductive crosslinked polyethylene , 1984 .

[17]  V. S. Prasad,et al.  The thermal and crystallisation studies of short sisal fibre reinforced polypropylene composites , 2003 .

[18]  M. Narkis,et al.  A preliminary investigation of conductive immiscible polymer blends as sensor materials , 2000 .

[19]  G. Beaucage,et al.  Morphology of Polyethylene-Carbon Black Composites , 1999 .

[20]  Model for thermal conductivities in spun yarn carbon fabric composites , 2005 .

[21]  Xuehong Lu,et al.  Thermal conductivity, electrical resistivity, mechanical, and rheological properties of thermoplastic composites filled with boron nitride and carbon fiber , 2005 .

[22]  Yong Zhang,et al.  Electrical properties and morphology of polypropylene/epoxy/glass fiber composites filled with carbon black , 2005 .

[23]  T. Chou,et al.  A general analytical model for predicting the transverse effective thermal conductivities of woven fabric composites , 1998 .

[24]  D. Bigg.  Mechanical and conductive properties of metal fibre-filled polymer composites , 1979 .

[25]  Jason M. Keith,et al.  Measuring and predicting in-plane thermal conductivity of carbon-filled nylon 6,6 polymer composites , 2006 .

[26]  R. Spontak,et al.  Volume‐exclusion effects in polyethylene blends filled with carbon black, graphite, or carbon fiber , 2002 .