论文信息 - On the origin of strain softening during deformation of aluminum in torsion to large strains

On the origin of strain softening during deformation of aluminum in torsion to large strains

An investigation of the evolution of the stress-strain curve during deformation in torsion has been carried out. The stress first increases to a narrow plateau, followed by a decrease in flow stress of about 20 pct until steady state is reached. In order to determine the factors that are responsible for the fall in flow stress, investigations of the microstructure and texture were made. The subgrain size was found to increase by about 20 pct corresponding to a fall in the flow stress of about 10 pct. The texture was found to change from a close to random texture at the peak of the flow stress to a texture mainly consisting of the components {001}〈110〉 and {112}〈110〉 at the strain where the stress-strain curve reaches the second steady state. A fall in the flow stress of about 5 pct could be ascribed to changes in texture occurring during deformation.

E. Nes | Erik Nes | Tanja Pettersen | T. Pettersen

[1] J. Jonas,et al. Equivalent strain in large deformation torsion testing : Theoretical and practical considerations , 1982 .

[2] J. Jonas,et al. Axial stresses and texture development during the torsion testing of Al, Cu and α-Fe , 1984 .

[3] H. Mcqueen,et al. Microstructural evolution in Al deformed to strains of 60 at 400°C , 1985 .

[4] John J. Jonas,et al. The Use of Torsion Testing to Assess Material Formability , 1982 .

[5] M. E. Kassner,et al. The dislocation microstructure of aluminum , 1987, Metallurgical and Materials Transactions A.

[6] H. Mcqueen,et al. Influence of ultra-high strains at elevated temperatures on the microstructure of aluminium. Part I , 1989 .

[7] J. R. Newby,et al. Formability of metallic materials - 2000 A. D , 1982 .

[8] M. E. Kassner,et al. Large-strain torsional deformation in aluminum at elevated temperatures , 1989 .

[9] H. Mcqueen,et al. Evolution of flow stress in aluminium during ultra-high straining at elevated temperatures. Part II , 1989 .

[10] K. Marthinsen,et al. Modeling the evolution in microstructure and properties during plastic deformation of f.c.c.-metals and alloys – an approach towards a unified model , 2002 .