Rebar corrosion in cracked RC prisms located in harsh marine environment

The aim of this paper is to evaluate the corrosion activity of cracked flexural reinforced concrete elements in a marine environment. Some non-destructive test results of a comprehensive research p...

[1]  M. Stern,et al.  Electrochemical Polarization I . A Theoretical Analysis of the Shape of Polarization Curves , 1957 .

[2]  Carolyn M. Hansson,et al.  Galvanostatic pulse technique with the current confinement guard ring: The laboratory and finite element analysis , 2008 .

[3]  Meysam Najimi,et al.  Transport properties of ternary concrete mixtures containing natural zeolite with silica fume or fly ash , 2014 .

[4]  V. Sirivivatnanon,et al.  Chloride diffusivity of concrete cracked in flexure , 2000 .

[5]  Mark Alexander,et al.  Modelling corrosion propagation in reinforced concrete structures – A critical review , 2011 .

[6]  Mohammad Shekarchi,et al.  Use of natural zeolite as a supplementary cementitious material , 2010 .

[7]  Hans Beushausen,et al.  Suitability of Various Measurement Techniques for Assessing Corrosion in Cracked Concrete , 2010 .

[8]  Jin Xia,et al.  Effect of chloride-induced reinforcing steel corrosion on the flexural strength of reinforced concrete beams , 2012 .

[9]  Ali Akbar Ramezanianpour,et al.  Assessment of service life models for determination of chloride penetration into silica fume concrete in the severe marine environmental condition , 2013 .

[10]  C. K. Larsen,et al.  Relationship between concrete resistivity and corrosion rate – A literature review , 2013 .

[11]  Hans Beushausen,et al.  Towards incorporating the influence of cover cracking on steel corrosion in RC design codes: the concept of performance-based crack width limits , 2012 .

[12]  Ali Akbar Ramezanianpour,et al.  Service Life Prediction of Silica Fume Concretes , 2007 .

[13]  Francisco Presuel-Moreno,et al.  Numerical modeling of the effects of rebar presence and/or multilayered concrete resistivity on the apparent resistivity measured via the Wenner method , 2013 .

[14]  Mohammad Shekarchi,et al.  Comparative studies of experimental and numerical techniques in measurement of corrosion rate and time-to-corrosion-initiation of rebar in concrete in marine environments , 2014 .

[15]  C. Andrade,et al.  Relation between resistivity and corrosion rate of reinforcements in carbonated mortar made with several cement types , 1988 .

[16]  Carolyn M. Hansson,et al.  The influence of cracks on chloride-induced corrosion of steel in ordinary Portland cement and high performance concretes subjected to different loading conditions , 2008 .

[17]  Hans Beushausen,et al.  Corrosion in cracked and uncracked concrete – influence of crack width, concrete quality and crack reopening , 2010 .

[18]  Michael Raupach,et al.  Half-cell potential measurements—Potential mapping on reinforced concrete structures , 2003 .

[19]  Ali Dousti,et al.  Influence of exposure temperature on chloride diffusion in concretes incorporating silica fume or natural zeolite , 2013 .