Investigation of Polished Single Crystal ZnO by Nanoindentation

Abstract The near surface mechanical response of polished single crystal ZnO has been investigated by nanoindentation. Surfaces of (0001) ZnO crystals were prepared by mechanical polishing with 1/4 μm and 1 μm diamond abrasives and by chemomechanical polishing. Values for the critical load at the onset of yielding, the elastic modulus and the depth dependent values of hardness were measured. Results were compared to etched (0001) surfaces and (0001bar), {101bar0} and {112bar0} surfaces which had been chemomechanically polished. Surface preparation and crystal orientation were both found to have an effect on the near surface mechanical response.

[1] Mathias Göken,et al. Pop-ins in Nanoindentations – the Initial Yield Point , 2001 .

[2] Jérôme Colin,et al. Pop-in phenomenon during nanoindentation in MgO , 1999 .

[3] D. Clarke,et al. Size dependent hardness of silver single crystals , 1995 .

[4] Herbert F. Wang,et al. Single Crystal Elastic Constants and Calculated Aggregate Properties. A Handbook , 1971 .

[5] N. L. Sizova,et al. Microhardness and Resistivity Anisotropy of ZnO Plastic Deformation , 1982 .

[6] G. Pharr,et al. An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments , 1992 .

[7] David C. Look,et al. Recent Advances in ZnO Materials and Devices , 2001 .

[8] T. J. Bell,et al. Recent Developments in Hardness Testing and their Implications for Standardisation , 1999 .

[9] S. Matsuoka,et al. Nanoindentation Measurement for a Tungsten(001)Single Crystal , 1998 .

[10] Peter M. Anderson,et al. Indentation induced dislocation nucleation: The initial yield point , 1996 .

[11] Hartmut S. Leipner,et al. Dislocation-related pop-in effect in gallium arsenide , 2001 .