Tuning roughness and gloss of powder coating paint by encapsulating the coating particles with thin Al2O3 films

In this work, we report a method to change the surface finish of a standard polyester-based powder coating paint, from gloss to matt, by depositing ultrathin films of Al2O3 on the powder coating particles. The coating experiments were performed in a fluidized bed reactor at 1 bar and 27 °C, using a gas-phase coating process of alternating exposure of the particles to the two precursors (trimethylaluminium and water), similar to atomic layer deposition (ALD). We varied the number of coating cycles (1, 2, 3, 5, 7 and 9 cycles) to obtain film thicknesses of the alumina shell ranging from 1 to 30 nm. The average growth per cycle of the process is 3.5 nm, significantly larger than the one for pure self-limiting ALD. When the average alumina shell was thicker than 6 nm, the shell prevented the flow of the core particles, even though the powder particles did soften above the glass transition temperature. With the particles morphology intact, this resulted in a rough and matte surface finish of the coating after curing. The surface roughness, with a value around 9 μm determined by surface profilometry, is associated to the alumina coated particles as observed with SEM and EDX analysis. In addition, the matte finish coating showed mechanical resistance similar to that of uncoated powder particles.

[1]  A. Laubengayer,et al.  The Alkyls of the Third Group Elements. I. Vapor Phase Studies of the Alkyls of Aluminum, Gallium and Indium1 , 1941 .

[2]  Roger T. Fenner,et al.  Mechanics of solids and structures , 1989 .

[3]  C. Detavernier,et al.  Reactor concepts for atomic layer deposition on agitated particles: A review , 2014 .

[4]  Arthur S. Morris,et al.  Thermo-Mechanical Properties of Alumina Films Created Using the Atomic Layer Deposition Technique , 2010 .

[5]  David Parker,et al.  Enhancing the activation of silicon carbide tracer particles for PEPT applications using gas-phase deposition of alumina at room temperature and atmospheric pressure , 2016 .

[6]  David Abend.  Mechanics Of Solids And Structures , 2016 .

[7]  G. Meesters,et al.  Gas-Phase Deposition of Ultrathin Aluminium Oxide Films on Nanoparticles at Ambient Conditions , 2015, Materials.

[8]  S. George,et al.  Barrier properties of polymer/alumina nanocomposite membranes fabricated by atomic layer deposition , 2008 .

[9]  S. George,et al.  Nucleation and Growth during Al2O3 Atomic Layer Deposition on Polymers , 2005 .

[10]  Alan W. Weimer,et al.  Atomic layer deposition of ultrathin and conformal Al2O3 films on BN particles , 2000 .

[11]  Mato Knez,et al.  Atomic layer deposition on biological macromolecules: metal oxide coating of tobacco mosaic virus and ferritin. , 2006, Nano letters.

[12]  J. N. Hay,et al.  A study of enthalpic relaxation of poly(ethylene terephthalate) by conventional and modulated temperature DSC , 2001 .

[13]  S. George.  Atomic layer deposition: an overview. , 2010, Chemical reviews.

[14]  Mikko Ritala,et al.  Crystallinity of inorganic films grown by atomic layer deposition: Overview and general trends , 2013 .

[15]  J. S. Price,et al.  Metal ALD and pulsed CVD: Fundamental reactions and links with solution chemistry , 2013 .

[16]  P. Li,et al.  Synthesis of oxidation-resistant metal nanoparticles via atomic layer deposition , 2007 .

[17]  A. Steinfeld,et al.  Surface Modification of Graphite Particles Coated by Atomic Layer Deposition and Advances in Ceramic Composites , 2013 .

[18]  B. Moghtaderi,et al.  Combustion Prevention of Iron Powders by a Novel Coating Method , 2006 .

[19]  J. Jur,et al.  Atomic layer deposition of Al(2)O(3) and ZnO at atmospheric pressure in a flow tube reactor. , 2011, ACS applied materials & interfaces.

[20]  Steven M. George,et al.  Critical tensile and compressive strains for cracking of Al2O3 films grown by atomic layer deposition , 2011 .

[21]  J. R. Ommen,et al.  Deposition Mechanism of Aluminum Oxide on Quantum Dot Films at Atmospheric Pressure and Room Temperature , 2016 .

[22]  D. King,et al.  Passivation of pigment-grade TiO2 particles by nanothick atomic layer deposited SiO2 films , 2008, Nanotechnology.

[23]  S. George,et al.  Low-Temperature Al2O3 Atomic Layer Deposition , 2004 .

[24]  Tosko Alexande Misev,et al.  Powder coatings technology: new developments at the turn of the century , 1998 .

[25]  C. Henrickson,et al.  Lewis acidity of alanes. Interactions of trimethylalane with sulfides , 1967 .

[26]  John Nijenhuis,et al.  Atmospheric Pressure Process for Coating Particles Using Atomic Layer Deposition , 2009 .

[27]  C. Detavernier,et al.  Aluminium atomic layer deposition applied to mesoporous zeolites for acid catalytic activity enhancement , 2011 .

[28]  S. S. Lee,et al.  Gloss reduction in low temperature curable hybrid powder coatings , 2003 .

[29]  Ivana K. Partridge,et al.  Investigation of cure induced shrinkage in unreinforced epoxy resin , 2002 .

[30]  R. G. Lees,et al.  Durable glossy, matte and wrinkle finish powder coatings crosslinked with tetramethoxymethyl glycoluril , 1996 .

[31]  Bruce Mayer,et al.  Transient analysis of carrier gas saturation in liquid source vapor generators , 2001 .

[32]  G. G. Stokes.  "J." , 1890, The New Yale Book of Quotations.

[33]  M. Mazumder,et al.  Gloss and Texture Control of Powder Coated Films , 2001 .

[34]  Riikka L. Puurunen,et al.  Growth Per Cycle in Atomic Layer Deposition: A Theoretical Model , 2003 .

[35]  Jyrki Vuorinen,et al.  Mechanical and tribological property comparison of melt-compounded nanocomposites of atomic-layer-deposition-coated polyamide particles and commercial nanofillers , 2009 .

[36]  Charles J. Wood,et al.  Novel Processing to Produce Polymer/Ceramic Nanocomposites by Atomic Layer Deposition , 2007 .

[37]  Tosko Aleksandar Misev,et al.  Powder Coatings: Chemistry and Technology , 1991 .

[38]  P. O’Brien,et al.  Atomic Layer Epitaxy , 2008 .

[39]  Álvaro Somoza,et al.  Synthesis and surface modification of uniform MFe2O4 (M = Fe, Mn, and Co) nanoparticles with tunable sizes and functionalities , 2012, Journal of Nanoparticle Research.

[40]  Functionalization of fine particles using atomic and molecular layer deposition , 2012 .

[41]  Jose Manuel Valverde,et al.  Fluidization of nanopowders: a review , 2012, Journal of Nanoparticle Research.

[42]  Jesse S. Jur,et al.  Effect of temperature and gas velocity on growth per cycle during Al2O3 and ZnO atomic layer deposition at atmospheric pressure , 2012 .

[43]  Energy-enhanced atomic layer deposition for more process and precursor versatility , 2013 .

[44]  J. R. Ommen,et al.  Scalable Production of Nanostructured Particles using Atomic Layer Deposition , 2014 .

[45]  L Mädler,et al.  Adhesion mechanisms of the contact interface of TiO2 nanoparticles in films and aggregates. , 2012, Langmuir : the ACS journal of surfaces and colloids.

[46]  Se Stephen Potts,et al.  Plasma-Assisted Atomic Layer Deposition: Basics, Opportunities, and Challenges , 2011 .

[47]  A. Weimer,et al.  Atomic layer deposited thin film metal oxides for fuel production in a solar cavity reactor , 2012 .

[48]  Alan W. Weimer,et al.  Nanocoating Individual Silica Nanoparticles by Atomic Layer Deposition in a Fluidized Bed Reactor , 2005 .

[49]  S. Or,et al.  Concurrent operational modes and enhanced current sensitivity in heterostructure of magnetoelectric ring and piezoelectric transformer , 2013 .

[50]  Victor M. Bright,et al.  The mechanical properties of atomic layer deposited alumina for use in micro- and nano-electromechanical systems , 2006 .

[51]  R. Puurunen.  Correlation between the growth-per-cycle and the surface hydroxyl group concentration in the atomic layer deposition of aluminum oxide from trimethylaluminum and water , 2005 .

[52]  S. Hatzikiriakos,et al.  Start-up pressure transients in a capillary rheometer , 1994 .

[53]  S. George,et al.  Conformal nanocoating of zirconia nanoparticles by atomic layer deposition in a fluidized bed reactor , 2005, Nanotechnology.

[54]  S. George,et al.  Nanocoating individual cohesive boron nitride particles in a fluidized bed by ALD , 2004 .