Damage Evolution in Al Wire Bonds Subjected to a Junction Temperature Fluctuation of 30 K

Ultrasonically bonded heavy Al wires subjected to a small junction temperature fluctuation under power cycling from 40°C to 70°C were investigated using a non-destructive three-dimensional (3-D) x-ray tomography evaluation approach. The occurrence of irreversible deformation of the microstructure and wear-out under such conditions were demonstrated. The observed microstructures consist of interfacial and inter-granular cracks concentrated in zones of stress intensity, i.e., near heels and emanating from interface precracks. Interfacial voids were also observed within the bond interior. Degradation rates of ‘first’ and ‘stitch’ bonds are compared and contrasted. A correlative microscopy study combining perspectives from optical microscopy with the x-ray tomography results clarifies the damage observed. An estimation of lifetime is made from the results and discussed in the light of existing predictions.

[1]  Z. F. Zhang,et al.  Fatigue cracking at twin boundaries: Effects of crystallographic orientation and stacking fault energy (vol 60, pg 3113, 2012) , 2012 .

[2]  James E. Krzanowski,et al.  A microstructural study of dislocation substructures formed in metal foil substrates during ultrasonic wire bonding , 1997 .

[3]  Bing Ji,et al.  In Situ Diagnostics and Prognostics of Wire Bonding Faults in IGBT Modules for Electric Vehicle Drives , 2013, IEEE Transactions on Power Electronics.

[4]  R. Pohlman,et al.  Influence of ultrasonic vibration on metallic friction , 1966 .

[5]  Kjeld Pedersen,et al.  Degradation Assessment in IGBT Modules Using Four-Point Probing Approach , 2015, IEEE Transactions on Power Electronics.

[6]  M. E. Kassner,et al.  Current issues in recrystallization: a review , 1997 .

[7]  Uwe Scheuermann,et al.  Impact of load pulse duration on power cycling lifetime of Al wire bonds , 2013, Microelectron. Reliab..

[8]  M. Thoben,et al.  Thermo-mechanical analysis of bonding wires in IGBT modules under operating conditions , 2012, Microelectron. Reliab..

[9]  N. Barbosa,et al.  Strain-Induced Grain Growth during Rapid Thermal Cycling of Aluminum Interconnects , 2007 .

[10]  Li Yang,et al.  Room-Temperature Nanoindentation Creep of Thermally Cycled Ultrasonically Bonded Heavy Aluminum Wires , 2013, Journal of Electronic Materials.

[11]  E. Maire,et al.  In Situ Experiments with X ray Tomography: an Attractive Tool for Experimental Mechanics , 2010 .

[12]  K. J. Miller,et al.  What is fatigue damage? A view point from the observation of low cycle fatigue process , 2005 .

[13]  James E. Krzanowski.  A transmission electron microscopy study of ultrasonic wire bonding , 1989 .

[14]  H. Reichl,et al.  Hardening and Softening in AlSi1 Bond Contacts During Ultrasonic Wire Bonding , 2009, IEEE Transactions on Components and Packaging Technologies.

[15]  Gerhard Wachutka,et al.  Crack mechanism in wire bonding joints , 1998 .

[16]  Golta Khatibi,et al.  Microstructural Investigation of Interfacial Features in Al Wire Bonds , 2012, Journal of Electronic Materials.

[17]  Masahiro Koizumi,et al.  Reliability of thick Al wire bonds in IGBT modules for traction motor drives , 2000 .

[18]  P. Sharma,et al.  Atomistic insights into dislocation-based mechanisms of void growth and coalescence , 2011 .

[19]  Z. G. Wang,et al.  Grain boundary effects on cyclic deformation and fatigue damage , 2008 .

[20]  Fausto Fantini,et al.  On the effect of power cycling stress on IGBT modules , 1998 .

[21]  Michael Mayer,et al.  Footprint study of ultrasonic wedge-bonding with aluminum wire on copper substrate , 2006 .

[22]  Marcus Sonner,et al.  Lifetime prediction of thick aluminium wire bonds for mechanical cyclic loads , 2014, Microelectron. Reliab..

[23]  Hiroyuki Kobayashi,et al.  Effects of grain boundary- and triple junction-character on intergranular fatigue crack nucleation in polycrystalline aluminum , 2008, Journal of Materials Science.

[24]  Mingwei Xu,et al.  Investigation of gate voltage oscillations in an IGBT module after partial bond wires lift-off , 2013, Microelectron. Reliab..

[25]  Reinhold Bayerer,et al.  Advanced packaging yields higher performance and reliability in power electronics , 2010, Microelectron. Reliab..

[26]  Yasushi Yamada,et al.  Reliability of wire-bonding and solder joint for high temperature operation of power semiconductor device , 2007, Microelectron. Reliab..

[27]  Golta Khatibi,et al.  Accelerated mechanical fatigue testing and lifetime of interconnects in microelectronics , 2010 .

[28]  P. Lukas,et al.  Role of persistent slip bands in fatigue , 2004 .

[29]  Mauro Ciappa,et al.  Selected failure mechanisms of modern power modules , 2002, Microelectron. Reliab..

[30]  M. Preuss,et al.  Fatigue and Damage in Structural Materials Studied by X-Ray Tomography , 2012 .

[31]  M. Held,et al.  Fast power cycling test for insulated gate bipolar transistor modules in traction application , 1999 .

[32]  P. Withers.  Mechanical failure: Imaging cracks in hostile regimes. , 2013, Nature materials.

[33]  C. C. Lee,et al.  Thermal-mechanical behavior of the bonding wire for a power module subjected to the power cycling test , 2011, Microelectron. Reliab..

[34]  P. Shanthraj,et al.  Dislocation-density mechanisms for void interactions in crystalline materials , 2012 .

[35]  T. Licht,et al.  A fast mechanical test technique for life time estimation of micro-joints , 2008, Microelectron. Reliab..