Experiments on shear deformation, debonding and local load transfer in a model graphite/glass/epoxy microcomposite

Recent statistical theories for the failure of polymer matrix composites depend heavily on details of the stress redistribution around fibre breaks. The magnitudes and length scales of fibre overloads as well as the extent of fibre/matrix debonding are key components in the development of longitudinal versus transverse crack propagation. While several theoretical studies have been conducted to investigate the roles of these mechanisms, little has been substantiated experimentally about the matrix constitutive behaviour and mechanisms of debonding at the length scale of a fibre break. In order to predict the growth of transverse and longitudinal cracks using the same micromechanical model, we microscopically observed the epoxy shear behaviour around a single fibre break in a three-fibre microcomposite tape. The planar specimens consisted of a single graphite fibre placed between two larger glass fibres in an epoxy matrix. The interfibre spacing was less than one fibre diameter (<6 μm) in order to reflect the spacing between fibres found in typical composites. The epoxy constitutive behaviour was modelled using shear-lag theory where the epoxy had elastic, plastic, and debond zones. The criteria for debonding were modified from conventional shear-lag approaches to reflect the orientational hardening in the epoxy network structure. The epoxy, which is brittle in bulk, locally underwent a shear strain of about 60% prior to debonding from the fibre.