Acoustic emission analysis of composite pressure vessels under constant and cyclic pressure

The use of acoustic emission (AE) for the detection of damage in carbon fibre composite pressure vessels was evaluated for constant and cyclic internal gas pressure loading conditions. AE was capable of monitoring the initiation and accumulation of damage events in a composite pressure vessel (CPVs), although it was not possible to reliably distinguish carbon fibre breakage from other microscopic damage events (e.g. matrix cracks, fibre/matrix interfacial cracks). AE tests performed on the carbon fibre laminate used as the skin of pressure vessels revealed that the development of damage is highly variable under constant pressure, with large differences in the rupture life and acoustic emission events at final failure. Numerical analysis of the skin laminate under constant tensile stress revealed that the high variability in the stress rupture life is due mainly to the stochastic behaviour of the carbon fibre rupture process.

[1]  Nathalie Godin,et al.  Clustering of acoustic emission signals collected during tensile tests on unidirectional glass/polyester composite using supervised and unsupervised classifiers , 2004 .

[2]  Kenjiro Komai,et al.  Investigations of the Fracture Mechanism of Carbon/Epoxy Composites by AE Signal Analyses , 1991 .

[3]  Kanji Ono,et al.  Acoustic Emission Behavior of Flawed Unidirectional Carbon Fiber-Epoxy Composites , 1988 .

[4]  A. Bunsell,et al.  Micromechanisms of load transfer in a unidirectional carbon fibre–reinforced epoxy composite due to fibre failures. Part 2: Influence of viscoelastic and plastic matrices on the mechanisms of load transfer , 2006 .

[5]  L. Dong,et al.  Acoustic emission monitoring of composite cylinders , 1997 .

[6]  R. Gaertner,et al.  Use of acoustic emission to identify damage modes in glass fibre reinforced polyester , 2002 .

[7]  Ian Sinclair,et al.  Damage accumulation in a carbon/epoxy composite: Comparison between a multiscale model and computed tomography experimental results , 2012 .

[8]  Alain Thionnet,et al.  Micromechanisms of load transfer in a unidirectional carbon fibre-reinforced epoxy composite due to fibre failures: Part 3. Multiscale reconstruction of composite behaviour , 2008 .

[9]  A. Bunsell,et al.  Effect of the loading rate on ultimate strength of composites. Application: Pressure vessel slow burst test , 2013 .

[10]  Ian Sinclair,et al.  Comparison of the accumulation of fibre breaks occurring in a unidirectional carbon/epoxy composite identified in a multi-scale micro-mechanical model with that of experimental observations using high resolution computed tomography , 2010 .

[11]  A. Scott,et al.  Advanced micromechanical analysis of highly loaded hybrid composite structures , 2009 .

[12]  T. Krietsch,et al.  Selection of acoustic emissions and classification of damage mechanisms in fiber composite materials , 1998 .

[13]  M. Benzeggagh,et al.  On the use of acoustic emission to investigate damage mechanisms in glass-fibre-reinforced polypropylene , 1994 .

[14]  A. Bunsell,et al.  Three-dimensional analysis of load transfer micro-mechanisms in fibre/matrix composites , 2009 .

[15]  Zhang Wei,et al.  Non-destructive Evaluation of Composite Pressure Vessel by Using FBG Sensors , 2007 .

[16]  Alain Thionnet,et al.  Visual indicator for the detection of end-of-life criterion for composite high pressure vessels for hydrogen storage , 2012 .

[17]  A. Bunsell,et al.  Fibre Break Failure Processes in Unidirectional Composites. Part 2: Failure and Critical Damage State Induced by Sustained Tensile Loading , 2015, Applied Composite Materials.

[18]  Wim De Waele,et al.  Monitoring of fibre reinforced composites with embedded optical fibre Bragg sensors, with application to filament wound pressure vessels , 2001 .

[19]  A. Bunsell,et al.  Micromechanisms of load transfer in a unidirectional carbon fibre–reinforced epoxy composite due to fibre failures. Part 1: Micromechanisms and 3D analysis of load transfer: The elastic case , 2006 .

[20]  K. Ono,et al.  Digital signal analysis of acoustic emission from carbon fiber/epoxy composites , 1990 .

[21]  B. Lung.  A structural health monitoring system for composite pressure vessels , 2005 .

[22]  A. Bunsell,et al.  Fibre Break Failure Processes in Unidirectional Composites. Part 3: Unidirectional Plies Included in Laminates , 2015, Applied Composite Materials.

[23]  Thomas Böhlke,et al.  Damage evolution and fracture events sequence in various composites by acoustic emission technique , 2007 .

[24]  Anthony R. Bunsell,et al.  Composite pressure vessels supply an answer to transport problems , 2006 .

[25]  A. Bunsell,et al.  Large strain cyclic fatigue testing of unidirectional carbon fibre reinforced epoxy resin , 2005 .

[26]  Chang-Kwon Moon,et al.  Fracture behavior of carbon fiber reinforced plastics determined by the time–frequency analysis method , 2003 .

[27]  H. Tsuda,et al.  Acoustic emission in carbon fibre-reinforced plastic materials , 2000 .

[28]  A. Bunsell,et al.  Damage accumulation processes and life prediction in unidirectional composites , 2007, Proceedings of the Royal Society A: Mathematical, Physical and Engineering Sciences.

[29]  Chun-Gon Kim,et al.  The embedment of fiber Bragg grating sensors into filament wound pressure tanks considering multiplexing , 2006 .

[30]  Jürgen Bohse,et al.  Acoustic emission characteristics of micro-failure processes in polymer blends and composites , 2000 .

[31]  Peter J. de Groot,et al.  Real-time frequency determination of acoustic emission for different fracture mechanisms in carbon/epoxy composites , 1995 .

[32]  Marvin A. Hamstad,et al.  Acoustic Emission from Depressurization to Detect/Evaluate Significance of Impact Damage to Graphite/Epoxy Pressure Vessels , 1998 .

[33]  Theodoros Loutas,et al.  On the characterization of continuous fibres fracture by quantifying acoustic emission and acousto-ultrasonics waveforms , 2004 .