Hydrogen sensing at room temperature with Pt-coated ZnO thin films and nanorods

A comparison is made of the sensitivities for detecting hydrogen with Pt-coated single ZnO nanorods and thin films of various thicknesses (20–350 nm). The Pt-coated single nanorods show a current response of approximately a factor of 3 larger at room temperature upon exposure to 500ppmH2 in N2 than the thin films of ZnO. The power consumption with both types of sensors can be very small (in the nW range) when using discontinuous coatings of Pt. Once the Pt coating becomes continuous, the current required to operate the sensors increases to the μW range. The optimum ZnO thin film thickness under our conditions was between 40–170 nm, with the hydrogen sensitivity falling off outside this range. The nanorod sensors show a slower recovery in air after hydrogen exposure than the thin films, but exhibit a faster response to hydrogen, consistent with the notion that the former adsorb relatively more hydrogen on their surface. Both ZnO thin and nanorods cannot detect oxygen.

[1]  Peidong Yang,et al.  Nanowire ultraviolet photodetectors and optical switches , 2002 .

[2]  Seonuk Park,et al.  Schottky nanocontacts on ZnO nanorod arrays , 2003 .

[3]  Ning Wang,et al.  FORMATION OF ZNO NANOSTRUCTURES BY A SIMPLE WAY OF THERMAL EVAPORATION , 2002 .

[4]  M. Meyyappan,et al.  Growth of Epitaxial Nanowires at the Junctions of Nanowalls , 2003, Science.

[5]  H. Hartnagel,et al.  Semiconducting Transparent Thin Films , 1995 .

[6]  David P. Norton,et al.  ZnO nanowire growth and devices , 2004 .

[7]  S. Noor Mohammad,et al.  InAs nanowires and whiskers grown by reaction of indium with GaAs , 2003 .

[8]  Gregory P. Harmer,et al.  Semiconducting metal oxide sensor array for the selective detection of combustion gases , 2003 .

[9]  Zhong Lin Wang.  Nanostructures of zinc oxide , 2004 .

[10]  Noritaka Usami,et al.  Optical properties of ZnO rods formed by metalorganic chemical vapor deposition , 2003 .

[11]  Jenshan Lin,et al.  Hydrogen-selective sensing at room temperature with ZnO nanorods , 2005 .

[12]  M. Meyyappan,et al.  Room temperature methane detection using palladium loaded single-walled carbon nanotube sensors , 2004 .

[13]  J. D. Sternhagen,et al.  Development of a micromachined hazardous gas sensor array , 2003 .

[14]  Jenshan Lin,et al.  Detection of hydrogen at room temperature with catalyst-coated multiple ZnO nanorods , 2005 .

[15]  Philip J. Poole,et al.  Spatially controlled, nanoparticle-free growth of InP nanowires , 2003 .

[16]  Gyu-Chul Yi,et al.  Quantum Confinement Observed in ZnO/ZnMgO Nanorod Heterostructures , 2003 .

[17]  Chenglu Lin,et al.  Fabrication and ethanol sensing characteristics of ZnO nanowire gas sensors , 2004 .

[18]  Zhong Lin Wang,et al.  Nanobelts of Semiconducting Oxides , 2001, Science.

[19]  Gyu-Chul Yi,et al.  Excitonic emissions observed in ZnO single crystal nanorods , 2003 .

[20]  Jih-Jen Wu,et al.  LOW-TEMPERATURE GROWTH OF WELL-ALIGNED ZNO NANORODS BY CHEMICAL VAPOR DEPOSITION , 2002 .

[21]  M. C. Horrillo,et al.  Hydrogen sensors based on carbon nanotubes thin films , 2005 .

[22]  Xingcai Wu,et al.  Crystalline gallium oxide nanowires: intensive blue light emitters , 2000 .

[23]  Q. Wan,et al.  Electronic transport through individual ZnO nanowires , 2004 .

[24]  Guanghai Li,et al.  Ordered indium-oxide nanowire arrays and their photoluminescence properties , 2001 .

[25]  S. Yu,et al.  Room-Temperature Ultraviolet Lasing from Zinc Oxide Microtubes , 2003 .

[26]  V. Varadarajan,et al.  Site-specific growth of Zno nanorods using catalysis-driven molecular-beam epitaxy , 2002 .

[27]  Yiying Wu,et al.  Room-Temperature Ultraviolet Nanowire Nanolasers , 2001, Science.

[28]  Chun-Sing Lee,et al.  Electrical properties of zinc oxide nanowires and intramolecular p–n junctions , 2003 .

[29]  Gyu-Tae Kim,et al.  Photocurrent in ZnO nanowires grown from Au electrodes , 2004 .

[30]  Jenshan Lin,et al.  Room-Temperature Hydrogen-Selective Sensing Using Single Pt-Coated ZnO Nanowires at Microwatt Power Levels , 2005 .

[31]  Hung-Ta Wang,et al.  Pt-coated InN nanorods for selective detection of hydrogen at room temperature , 2005 .