论文信息 - Chloride diffusion in concrete subjected to compressive loading

Chloride diffusion in concrete subjected to compressive loading

The influence of lateral surface microcracking on chloride diffusion in ordinary concrete (OC) and high-performance concrete (HPC) was investigated. The development of microcracks in the concretes was described by an evaluation indicator calculated from strain measurements at macroscopic level. Concrete specimens were subjected to monotonic or cyclic loading to different loading levels and then long-term chloride bulk diffusion tests were carried out on compressed specimens with only one exposed lateral surface. The effect of compressive loading on the chloride diffusion coefficient was analysed by means of the specific crack area. The results indicate that an increase in compressive loading increases the chloride diffusion coefficient and the effect is more obvious in OC than HPC. However, compared with OC, the chloride diffusion coefficient of HPC is more sensitive to microcracking in the lateral surface.

[1] Kefei Li,et al. Characterizing the effect of compressive damage on transport properties of cracked concretes , 2012 .

[2] H. Ishimori,et al. Chloride permeability of concrete under static and repeated compressive loading , 1995 .

[3] Gilles Pijaudier-Cabot,et al. Effects and interactions of temperature and stress-level related damage on permeability of concrete , 2007 .

[4] Nemkumar Banthia,et al. The effect of mechanical stress on permeability of concrete : A review , 2009 .

[5] N. Gowripalan,et al. Microcracking and chloride permeability of concrete under uniaxial compression , 2000 .

[6] Shamsad Ahmad. Reinforcement corrosion in concrete structures, its monitoring and service life prediction - A review , 2003 .

[7] Y. Loo. A new method for microcrack evaluation in concrete under compression , 1992 .

[8] Geert De Schutter,et al. Non-steady state chloride diffusion in concrete with different crack densities , 2013 .

[9] Stéphanie Bonnet,et al. Influence of traversing crack on chloride diffusion into concrete , 2008 .

[10] Wu-man Zhang,et al. Chloride diffusion coefficient and service life prediction of concrete subjected to repeated loadings , 2013 .

[11] Surendra P. Shah,et al. Effect of Cracking on Water and Chloride Permeability of Concrete , 1999 .

[12] O. Rodríguez,et al. INFLUENCE OF CRACKS ON CHLORIDE INGRESS INTO CONCRETE , 2003 .

[13] N. Banthia,et al. Permeability of concrete under stress , 2005 .