Effect of pulsed current and post weld aging treatment on tensile properties of argon arc welded high strength aluminium alloy

This paper reveals the effect of pulsed current and post weld aging treatment on tensile properties of argon arc welded AA7075 aluminium alloy. This alloy has gathered wide acceptance in the fabrication of light weight structures requiring high strength-to-weight ratio, such as transportable bridge girders, military vehicles, road tankers and railway transport systems. The preferred welding processes of high strength aluminium alloy are frequently gas tungsten arc welding (GTAW) process and gas metal arc welding (GMAW) process due to their comparatively easier applicability and better economy. Weld fusion zones typically exhibit coarse columnar grains because of the prevailing thermal conditions during weld metal solidification. This often results inferior weld mechanical properties and poor resistance to hot cracking. In this investigation, an attempt has been made to refine the fusion zone grains by applying pulsed current welding technique. Four different welding techniques have been used to fabricate the joints and they are: (i) continuous current GTAW (CCGTAW), (ii) pulsed current GTAW (PCGTAW), (iii) continuous current GMAW (CCGMAW) and (iv) pulsed current GMAW (PCGMAW) processes. As welded joint strength is much lower than the base metal strength and hence, a simple aging treatment has been given to improve the tensile strength of the joints. Current pulsing leads to relatively finer and more equi-axed grain structure in GTA and GMA welds. In contrast, conventional continuous current welding resulted in predominantly columnar grain structures. Post weld aging treatment is accompanied by an increase in tensile strength and tensile ductility.

[1]  G. Madhusudhan Reddy,et al.  Optimisation of pulse frequency in pulsed current gas tungsten arc welding of aluminium–lithium alloy sheets , 1998 .

[2]  Hwan Tae Kim,et al.  Solidification cracking susceptibility of high strength aluminum alloy weldment , 1996 .

[3]  G. Madhusudhan Reddy,et al.  Influence of scandium on weldability of 7010 aluminium alloy , 2005 .

[4]  P. K. Ghosh,et al.  Chemical Composition and Microstucture in Pulsed MIG Welded Al–Zn–Mg Alloy , 1991 .

[5]  Guo-xiang Wang,et al.  A mechanism for the formation of equiaxed grains in welds of aluminum–lithium alloy 2090 , 2003 .

[6]  X. Z. Li,et al.  GP-zones in Al–Zn–Mg alloys and their role in artificial aging , 2001 .

[7]  T. Mohandas,et al.  Effect of frequency of pulsing in gas tungsten arc welding on the microstructure and mechanical properties of titanium alloy welds: A technical note , 1996 .

[8]  G. Reddy,et al.  Weld microstructure refinement in a 1441 grade aluminium-lithium alloy , 1997 .

[9]  G. Reddy,et al.  Gas tungsten arc welding studies on similar and dissimilar combinations of Al-Zn-Mg alloy RDE 40 and Al-Li alloy 1441 , 2002 .

[10]  J. M. Vitek,et al.  Correlation between solidification parameters and weld microstructures , 1989 .

[11]  G. Ram,et al.  Microstructural refinement through inoculation of type 7020 Al–Zn–Mg alloy welds and its effect on hot cracking and tensile properties , 2003 .

[12]  M. Kamaraj,et al.  Improving mechanical properties of 2219 aluminium alloy GTA welds by scandium addition , 2005 .