Microwave‐sintered 3D printed tricalcium phosphate scaffolds for bone tissue engineering

This study reports the manufacturing process of 3D interconnected macroporous tricalcium phosphate (TCP) scaffolds with controlled internal architecture by direct 3D printing (3DP), and high mechanical strength obtained by microwave sintering. TCP scaffolds with 27%, 35% and 41% designed macroporosity with pore sizes of 500 μm, 750 μm and 1000 μm, respectively, were manufactured by direct 3DP. These scaffolds were then sintered at 1150 °C and 1250 °C in conventional electric muffle and microwave furnaces, respectively. Total open porosity between 42% and 63% was obtained in the sintered scaffolds due to the presence of intrinsic micropores along with designed pores. A significant increase in compressive strength between 46% and 69% was achieved by microwave compared to conventional sintering as a result of efficient densification. Maximum compressive strengths of 10.95 ± 1.28 MPa and 6.62 ± 0.67 MPa were achieved for scaffolds with 500 μm designed pores (~ 400 μm after sintering) sintered in microwave and conventional furnaces, respectively. An increase in cell density with a decrease in macropore size was observed during in vitro cell‐material interactions using human osteoblast cells. Histomorphological analysis revealed that the presence of both micro‐ and macropores facilitated osteoid‐like new bone formation when tested in femoral defects of Sprague–Dawley rats. Our results show that bioresorbable 3D‐printed TCP scaffolds have great potential in tissue engineering applications for bone tissue repair and regeneration. Copyright © 2012 John Wiley & Sons, Ltd.

[1]  Jiang Chang,et al.  Improvement of mechanical properties of macroporous β-tricalcium phosphate bioceramic scaffolds with uniform and interconnected pore structures , 2011 .

[2]  M. Cima,et al.  Three-Dimensional Printing: Rapid Tooling and Prototypes Directly from a CAD Model , 1990 .

[3]  Sergey V. Dorozhkin,et al.  Calcium orthophosphates , 2007 .

[4]  Gabriele Grimm,et al.  Development of a new calcium phosphate powder-binder system for the 3D printing of patient specific implants , 2007, Journal of materials science. Materials in medicine.

[5]  K. de Groot.  Effect of porosity and physicochemical properties on the stability, resorption, and strength of calcium phosphate ceramics. , 1988, Annals of the New York Academy of Sciences.

[6]  Emanuel M. Sachs,et al.  Three Dimensional Printing: Rapid Tooling and Prototypes Directly from CAD Representation , 1990 .

[7]  J. Davies,et al.  Engineering three-dimensional bone tissue in vitro using biodegradable scaffolds: investigating initial cell-seeding density and culture period. , 2000, Journal of biomedical materials research.

[8]  S. Kalita,et al.  Fabrication of 3-D Porous Mg/Zn doped Tricalcium Phosphate Bone-Scaffolds via the Fused Deposition Modelling , 2006 .

[9]  K. Nguyen,et al.  A review of materials, fabrication methods, and strategies used to enhance bone regeneration in engineered bone tissues. , 2008, Journal of biomedical materials research. Part B, Applied biomaterials.

[10]  Amit Bandyopadhyay,et al.  Pore size and pore volume effects on alumina and TCP ceramic scaffolds , 2003 .

[11]  P. Gatenholm,et al.  Influence of pore size on the redifferentiation potential of human articular chondrocytes in poly(urethane urea) scaffolds , 2011, Journal of tissue engineering and regenerative medicine.

[12]  R. V. Prasad,et al.  Synthesis and sintered properties evaluation of calcium phosphate ceramics , 2007 .

[13]  J. Chevalier,et al.  Effect of micro- and macroporosity of bone substitutes on their mechanical properties and cellular response , 2003, Journal of materials science. Materials in medicine.

[14]  P H Krebsbach,et al.  Indirect solid free form fabrication of local and global porous, biomimetic and composite 3D polymer-ceramic scaffolds. , 2003, Biomaterials.

[15]  P. D. de Oliveira,et al.  Pore size regulates cell and tissue interactions with PLGA–CaP scaffolds used for bone engineering , 2012, Journal of tissue engineering and regenerative medicine.

[16]  Julia Will,et al.  Porous ceramic bone scaffolds for vascularized bone tissue regeneration , 2008, Journal of materials science. Materials in medicine.

[17]  D. Hutmacher,et al.  Scaffolds in tissue engineering bone and cartilage. , 2000, Biomaterials.

[18]  K. Leong,et al.  The design of scaffolds for use in tissue engineering. Part II. Rapid prototyping techniques. , 2002, Tissue engineering.

[19]  A. Bandyopadhyay,et al.  Calcium Phosphate‐Based Resorbable Ceramics: Influence of MgO, ZnO, and SiO2 Dopants , 2006 .

[20]  S F Hulbert,et al.  Potential of ceramic materials as permanently implantable skeletal prostheses. , 1970, Journal of biomedical materials research.

[21]  Wei Sun,et al.  Computer‐aided tissue engineering: application to biomimetic modelling and design of tissue scaffolds , 2004, Biotechnology and applied biochemistry.

[22]  R. Carrodeguas,et al.  α-Tricalcium phosphate: synthesis, properties and biomedical applications. , 2010, Acta biomaterialia.

[23]  Chaozong Liu,et al.  Design and Development of Three-Dimensional Scaffolds for Tissue Engineering , 2007 .

[24]  K. Leong,et al.  The design of scaffolds for use in tissue engineering. Part I. Traditional factors. , 2001, Tissue engineering.

[25]  A. Bandyopadhyay,et al.  Strength Degradation of Nonrandom Porous Ceramic Structures under Uniaxial Compressive Loading , 2004 .

[26]  A. Bandyopadhyay,et al.  Understanding the influence of MgO and SrO binary doping on the mechanical and biological properties of beta-TCP ceramics. , 2010, Acta biomaterialia.

[27]  Miqin Zhang,et al.  Biphasic calcium phosphate nanocomposite porous scaffolds for load-bearing bone tissue engineering. , 2004, Biomaterials.

[28]  M Bohner,et al.  Structural and material approaches to bone tissue engineering in powder-based three-dimensional printing. , 2011, Acta biomaterialia.

[29]  E. Sachlos,et al.  Making tissue engineering scaffolds work. Review: the application of solid freeform fabrication technology to the production of tissue engineering scaffolds. , 2003, European cells & materials.

[30]  Amit Bandyopadhyay,et al.  Microwave-processed nanocrystalline hydroxyapatite: simultaneous enhancement of mechanical and biological properties. , 2010, Acta biomaterialia.

[31]  A. Bandyopadhyay,et al.  Microwave sintering of calcium phosphate ceramics , 2009 .

[32]  H. Takita,et al.  Geometry of Carriers Controlling Phenotypic Expression in BMP-Induced Osteogenesis and Chondrogenesis , 2001, The Journal of bone and joint surgery. American volume.

[33]  R. Roy,et al.  Microwave sintering of Ni–Zn ferrites: comparison with conventional sintering , 2003 .

[34]  U. Holzwarth,et al.  Effect of surface finish on the osseointegration of laser-treated titanium alloy implants. , 2004, Biomaterials.

[35]  A. L. Ortiz,et al.  Clarifying the effect of sintering conditions on the microstructure and mechanical properties of β-tricalcium phosphate , 2010 .

[36]  S. Hollister.  Porous scaffold design for tissue engineering , 2005, Nature materials.

[37]  Yunzhi Yang,et al.  Novel template-casting technique for fabricating beta-tricalcium phosphate scaffolds with high interconnectivity and mechanical strength and in vitro cell responses. , 2009, Journal of biomedical materials research. Part A.

[38]  常江,et al.  Improvement of mechanical properties of macroporous b-tricalcium phosphate bioceramic scaffolds with uniform and interconnected pore structures , 2011 .

[39]  Erhan Pişkin,et al.  Three-dimensional ingrowth of bone cells within biodegradable cryogel scaffolds in bioreactors at different regimes. , 2008, Tissue engineering. Part A.

[40]  Pamela Habibovic,et al.  Osteoinductive biomaterials—properties and relevance in bone repair , 2007, Journal of tissue engineering and regenerative medicine.