Effect of Ion Current Density on the Properties of Vacuum Arc-Deposited TiN Coatings

The influence of ion current density on the thickness of coatings deposited in a vacuum arc setup has been investigated to optimize the coating porosity. A planar probe was used to measure the ion current density distribution across plasma flux. A current density from 20 to 50 A/m2 was obtained, depending on the probe position relative to the substrate center. TiN coatings were deposited onto the cutting inserts placed at different locations on the substrate, and SEM was used to characterize the surfaces of the coatings. It was found that low-density coatings were formed at the decreased ion current density. A quantitative dependence of the coating thickness on the ion current density in the range of 20-50 A/m2 were obtained for the films deposited at substrate bias of 200 V and nitrogen pressure 0.1 Pa, and the coating porosity was calculated. The coated cutting inserts were tested by lathe machining of the martensitic stainless steel AISI 431. The results may be useful for controlling ion flux distribution over large industrial-scale substrates.

[1]  Yuan Pan,et al.  A single electrode room-temperature plasma jet device for biomedical applications , 2008 .

[2]  Zhengyi Jiang,et al.  Cavitation erosion resistance of NiTi thin films produced by Filtered Arc Deposition , 2009 .

[3]  André Anders,et al.  Handbook of plasma immersion ion implantation and deposition , 2004 .

[4]  I. Denysenko,et al.  Formation of vertically aligned carbon nanostructures in plasmas: numerical modelling of growth and energy exchange , 2011 .

[5]  S. Goldsmith,et al.  Interaction of a vacuum arc plasma beam with an obstacle positioned normal to the plasma flow , 2003 .

[6]  Kostya Ostrikov,et al.  Effective control of ion fluxes over large areas by magnetic fields : from narrow beams to highly uniform fluxes , 2009 .

[7]  Chang Q. Sun,et al.  Effects of substrate bias and growth temperature on properties of aluminium oxide thin films by using filtered cathodic vacuum arc , 2005 .

[8]  K. Ostrikov.  Plasma Nanoscience: Basic Concepts and Applications of Deterministic Nanofabrication , 2008 .

[9]  Jane P. Chang,et al.  Lecture Notes on Principles of Plasma Processing , 2003 .

[10]  Control of Surface Degradation on Biodegradable Magnesium Alloys by Plasma-Based Technology , 2013, IEEE Transactions on Plasma Science.

[11]  B. Ganguly,et al.  Plasma jets and and plasma bullets , 2012 .

[12]  Oleg Baranov,et al.  Current Distribution on the Substrate in a Vacuum Arc Deposition Setup , 2008 .

[13]  M. Mozetič,et al.  Reactive oxygen plasma-enabled synthesis of nanostructured CdO: tailoring nanostructures through plasma–surface interactions , 2008, Nanotechnology.

[14]  K. Ostrikov,et al.  Sustainable Nanoscience for a Sustainable Future , 2013, IEEE Transactions on Plasma Science.

[15]  Michael G. Kong,et al.  Plasma jets and plasma bullets , 2012 .

[16]  S. Goldsmith,et al.  Transport of a vacuum arc plasma beam through the aperture of an annular anode , 2005, IEEE Transactions on Plasma Science.

[17]  S. Mändl,et al.  Thin Film Deposition Using Energetic Ions , 2010, Materials.

[18]  Bengkang Tay,et al.  Electrowetting control of Cassie-to-Wenzel transitions in superhydrophobic carbon nanotube-based nanocomposites. , 2009, ACS nano.

[19]  M. Meyyappan,et al.  Plasma nanoscience: from nano-solids in plasmas to nano-plasmas in solids , 2013, 1306.6711.

[20]  A. Murphy,et al.  Plasma nanoscience: setting directions, tackling grand challenges , 2011 .

[21]  Oleg Baranov,et al.  Process Intensification in Vacuum Arc Deposition Setups , 2009 .

[22]  Shuyan Xu,et al.  Plasma-Aided Nanofabrication: From Plasma Sources to Nanoassembly , 2007 .

[23]  Jinghua Fang,et al.  Control of ion density distribution by magnetic traps for plasma electrons , 2012 .

[24]  Wei Zhou,et al.  Low temperature deposition of nanocrystalline TiO2 films: enhancement of nanocrystal formation by energetic particle bombardment , 2007 .

[25]  Michael Keidar,et al.  Ion current distribution on a substrate during nanostructure formation , 2004 .

[26]  Young-Seok Kim,et al.  Development of preferred orientation in polycrystalline NaCl-structure δ-TaN layers grown by reactive magnetron sputtering: Role of low-energy ion surface interactions , 2002 .