Molecular Confinement Accelerates Deformation of Entangled Polymers During Squeeze Flow

The squeezing of polymers in narrow gaps is important for the dynamics of nanostructure fabrication by nanoimprint embossing and the operation of polymer boundary lubricants. We measured stress versus strain behavior while squeezing entangled polystyrene films to large strains. In confined conditions where films were prepared to a thickness less than the size of the bulk macromolecule, resistance to deformation was markedly reduced for both solid-glass forging and liquid-melt molding. For melt flow, we further observed a complete inversion of conventional polymer viscosity scaling with molecular weight. Our results show that squeeze flow is accelerated at small scales by an unexpected influence of film thickness in polymer materials.

[1]  Christopher J. Ellison,et al.  The distribution of glass-transition temperatures in nanoscopically confined glass formers , 2003, Nature materials.

[2]  P. Duxbury,et al.  Multifunctional nanocomposites with reduced viscosity , 2007 .

[3]  L. Jay Guo,et al.  Recent progress in nanoimprint technology and its applications , 2004 .

[4]  C. Servais,et al.  Squeeze flow theory and applications to rheometry: A review , 2005 .

[5]  Helmut Schift,et al.  Flow behaviour of thin polymer films used for hot embossing lithography , 2000 .

[6]  S. Granick,et al.  Nanorheology of Confined Polymer Melts. 3. Weakly Adsorbing Surfaces , 1994 .

[7]  H. Brown,et al.  Chain entanglement in thin freestanding polymer films. , 2005, Physical review letters.

[8]  Amy Cha-Tien Sun,et al.  Impact of polymer film thickness and cavity size on polymer flow during embossing: toward process design rules for nanoimprint lithography , 2005 .

[9]  Willi Volksen,et al.  A buckling-based metrology for measuring the elastic moduli of polymeric thin films , 2004, Nature materials.

[10]  H. Brown,et al.  Entanglements at Polymer Surfaces and Interfaces , 1996 .

[11]  T. Hufnagel,et al.  Mechanical behavior of amorphous alloys , 2007 .

[12]  J. Frommer,et al.  Interfacial glass transition profiles in ultrathin, spin cast polymer films. , 2004, The Journal of chemical physics.

[13]  Shi‐Qing Wang,et al.  Banding in entangled polymer fluids under oscillatory shearing. , 2006, Physical review letters.

[14]  R. Jones,et al.  Character of the glass transition in thin supported polymer films. , 2001, Physical review. E, Statistical, nonlinear, and soft matter physics.

[15]  C. Tsenoglou.  Non-Newtonian Rheology of Entangled Polymer Solutions and Melts , 2001 .

[16]  O. Hassager,et al.  Extensional viscosity for polymer melts measured in the filament stretching rheometer , 2003 .

[17]  Hugh R. Brown,et al.  Polymer Mobility In Thin Films , 1996 .

[18]  Hella-Christin Scheer,et al.  Strategies for wafer-scale hot embossing lithography , 2001, European Mask and Lithography Conference.

[19]  G. Cross,et al.  Influence of elastic strains on the mask ratio in glassy polymer nanoimprint , 2005 .

[20]  J. Li,et al.  Slip processes in the deformation of polystyrene , 1976 .

[21]  Joseph L. Keddie,et al.  Size-Dependent Depression of the Glass Transition Temperature in Polymer Films , 1994 .

[22]  O. Hassager,et al.  Elongational viscosity of monodisperse and bidisperse polystyrene melts , 2006 .

[23]  S. Chou,et al.  Imprint Lithography with 25-Nanometer Resolution , 1996, Science.

[24]  Stephen R. Forrest,et al.  The path to ubiquitous and low-cost organic electronic appliances on plastic , 2004, Nature.

[25]  G. Cross,et al.  The production of nanostructures by mechanical forming , 2006 .

[26]  G. Cross,et al.  Variable temperature thin film indentation with a flat punch. , 2008, The Review of scientific instruments.

[27]  G. Cross,et al.  Measuring glassy and viscoelastic polymer flow in molecular-scale gaps using a flat punch mechanical probe. , 2008, ACS nano.