Sensitivity of the two-dimensional electric potential/resistance method for damage monitoring in carbon fiber polymer-matrix composite

The two-dimensional electric potential/resistance method is much less sensitive than the one-dimensional resistance method for damage monitoring in carbon fiber polymer-matrix composite. In the two-dimensional method, the resistance measurement is more sensitive than the potential gradient measurement. The sensitivity of the potential method is enhanced when the potential gradient line is close to the current line.

[1]  Xiaojun Wang,et al.  Sensing delamination in a carbon fiber polymer-matrix composite during fatigue by electrical resistance measurement , 1997 .

[2]  A. Chateauminois,et al.  In situ detection of damage in CFRP laminates by electrical resistance measurements , 1999 .

[3]  Martine Wevers,et al.  Optical and acoustic damage detection in laminated CFRP composite materials , 2000 .

[4]  Gerhard Mook,et al.  Non-destructive characterization of smart CFRP structures , 2003 .

[5]  D.D.L. Chung,et al.  Mechanical damage in carbon fiber polymer-matrix composite, studied by electrical resistance measurement , 2002 .

[6]  Karl Schulte,et al.  Non-destructive testing of FRP by d.c. and a.c. electrical methods , 2001 .

[7]  D. Chung,et al.  Effects of composite lay-up configuration and thickness on the damage self-sensing behavior of carbon fiber polymer-matrix composite , 2005 .

[8]  Karl Schulte,et al.  Load and failure analyses of CFRP laminates by means of electrical resistivity measurements , 1989 .

[9]  D. Chung,et al.  Thermal Fatigue in Carbon Fibre Polymer-Matrix Composites, Monitored in Real Time by Electrical Resistance Measurements , 2001 .

[10]  Dong-Jin Yoon,et al.  Nondestructive damage detection and interfacial evaluation of single-fibers/epoxy composites using PZT, PVDF and P(VDF-TrFE) copolymer sensors , 2005 .

[11]  Xiaojun Wang,et al.  Sensing damage in carbon fiber and its polymer-matrix and carbon-matrix composites by electrical resistance measurement , 1999 .

[12]  S. Al-Hassani,et al.  ELECTRICAL RESISTANCE MEASUREMENT TECHNIQUE FOR DETECTING FAILURE IN CFRP MATERIALS AT HIGH STRAIN RATES , 1994 .

[13]  G. Giraud,et al.  In-situ monitoring of damage in CFRP laminates by means of AC and DC measurements , 2001 .

[14]  C. Li,et al.  Composite Materials (I) , 1975 .

[15]  Akira Todoroki,et al.  Electrical resistance change method for monitoring delaminations of CFRP laminates: effect of spacing between electrodes , 2005 .

[16]  D. Chung,et al.  Self-sensing of Damage and Strain in Carbon Fiber Polymer-Matrix Structural Composites by Electrical Resistance Measurement , 2003 .

[17]  M. Kakihana,et al.  Materials Research Society Symposium - Proceedings , 2000 .

[18]  Jaycee H. Chung,et al.  Self-sensing of damage in carbon fiber polymer-matrix composite by measurement of the electrical resistance or potential away from the damaged region , 2005 .

[19]  Phil E. Irving,et al.  Experimental and finite element study of the electrical potential technique for damage detection in CFRP laminates , 2005 .

[20]  Nondestructive Evaluation Technique Utilizing Embedded Thermal Fiber Optic Sensors , 2003 .

[21]  Jaycee H. Chung,et al.  Impact damage of carbon fiber polymer-matrix composites, studied by electrical resistance measurement , 2005 .

[22]  M. Miyayama,et al.  Foreseeing of Fracture in CFGFRP Composites by the Measurement of Residual Change in Electrical Resistance , 1992 .

[23]  Simon A. Hayes,et al.  A resistance-based damage location sensor for carbon-fibre composites , 2002 .

[24]  J.E.T. Penny,et al.  Impact Location on Stiffened Composite Structures Using Neural Networks , 2001 .

[25]  Teruyuki Nakatsuji,et al.  Design of intelligent materials with self-diagnosing function for preventing fatal fracture , 1992 .

[26]  Francesco Aymerich,et al.  Ultrasonic evaluation of matrix damage in impacted composite laminates , 2000 .

[27]  Hiroaki Yanagida,et al.  Materials design of CFGFRP-reinforced concretes with diagnosing function for preventing fatal fracture , 1995 .

[28]  Akira Todoroki,et al.  Electrical Resistance Change of Unidirectional CFRP Due to Applied Load , 2004 .

[29]  Xiaojun Wang,et al.  Fiber breakage in polymer-matrix composite during static and fatigue loading, observed by electrical resistance measurement , 1999 .

[30]  Jaycee H. Chung,et al.  Self-sensing of Damage in Carbon Fiber Polymer–Matrix Composite Cylinder by Electrical Resistance Measurement , 2006 .

[31]  D.D.L. Chung,et al.  Real-time monitoring of fatigue damage and dynamic strain in carbon fiber polymer-matrix composite by electrical resistance measurement , 1997 .

[32]  L. Vincent,et al.  Damage mechanisms characterisation of carbon fibre/epoxy composite laminates by both electrical resistance measurements and acoustic emission analysis , 1996 .

[33]  D. Chung,et al.  The interlaminar interface of a carbon fiber epoxy-matrix composite as an impact sensor , 2005 .

[34]  Phil E. Irving,et al.  Fatigue damage characterization in carbon fibre composite materials using an electrical potential technique , 1998 .

[35]  R. Prabhakaran,et al.  Damage assessment through electrical resistance measurement in graphite fiber-reinforced composites , 1990 .

[36]  Akira Todoroki,et al.  Multi-prove electric potential change method for delamination monitoring of graphite/epoxy composite plates using normalized response surfaces , 2004 .