论文信息 - Dissolution of MgO in CaO–“FeO”–CaF2–SiO2 Slags under Static Conditions

Dissolution of MgO in CaO–“FeO”–CaF2–SiO2 Slags under Static Conditions

The dissolution of MgO in CaO–“FeO”–CaF2–SiO2 slags has been studied in the temperature range 1573°–1673° K under static conditions. The concentration profiles of Mg in the product Mg1-xFexO solid-solution layer as well as slag were determined by EDS analysis. From this, the diffusivities of MgO in the slag and the. interdiffusivities in solid solution were estimated. The dissolution of MgO in CaO–“FeO”–CaF2–SiO2 slags increased with CaF2 content.

S. Seetharaman | Ping Zhang

[1] E. Ichise,et al. Activities of FexO in CaO + CaF2 + SiO2 + FexO quaternary slags by disposable electrochemical oxygen probes , 1986 .

[2] P. Mellberg,et al. An Electrochemical Study of Silica Diffusion in Liquid CaO-SiO2-Al2O3-CaF2 Slags , 1981 .

[3] G. Yurek,et al. Deviations from Local Thermodynamic Equilibrium During Interdiffusion of CoOMgO and CoONiO , 1975 .

[4] M. Shimoji,et al. Effect of alkali and alkaline-earth fluorides on surface tension of molten calcium silicates , 1970 .

[5] J. A. Pask,et al. Diffusion of Iron and Nickel in Magnesium Oxide Single Crystals , 1969 .

[6] Marvin Appel. Solution for Fick's 2nd law with variable diffusivity in a multi-phase system , 1968 .

[7] T. Katsura,et al. Equilibria in the System FeO–Fe2O3–MgO at 1160°C , 1965 .

[8] E. Rigby,et al. Interdiffusion Studies of the System FexO-MgO , 1965 .

[9] D. J. Williams,et al. Effect of fluorides on silicates and phosphates , 1961 .