Improving field-emission uniformity of large-area W18O49 nanowire films by electrical treatment

W18O49 nanowires exhibit stable field emission at low fields. To explore the potential application of such nanowires in backlight and display devices, it is necessary to achieve uniform emission on a large area. In the present study, the authors demonstrate that field-emission uniformity of large-area samples may be improved by following an electrical-current treatment procedure. This is due to the increase in the number of nanowires that join in the field emission during the process, in which a small number of strong emitters are gradually melted down. The process of self-melting occurring in field emission is studied using a point anode in situ with a scanning electron microscope. The self-melting is attributed to the effect of Joule heating occurring due to passing of current through field electron emitting nanowires. These results are useful for the device application of W18O49 nanowires as large-area cold cathodes.

[1]  C. Chu,et al.  Uniformity enhancement of carbon nanofiber emitters via electrical discharge machining , 2007 .

[2]  E. Wang,et al.  Tuning the field-emission properties of tungsten oxide nanorods. , 2005, Small.

[3]  S. Jo,et al.  Field emission of zinc oxide nanowires grown on carbon cloth , 2004 .

[4]  Xiao Wei Sun,et al.  Field emission from zinc oxide nanopins , 2003 .

[5]  Jun Chen,et al.  Growth and field-emission property of tungsten oxide nanotip arrays , 2005 .

[6]  Lih-Juann Chen,et al.  Nitrogen-doped tungsten oxide nanowires: low-temperature synthesis on Si, and electrical, optical, and field-emission properties. , 2007, Small.

[7]  Jun Chen,et al.  On achieving better uniform carbon nanotube field emission by electrical treatment and the underlying mechanism , 2006 .

[8]  Jun Chen,et al.  Mechanism responsible for initiating carbon nanotube vacuum breakdown. , 2004, Physical review letters.

[9]  Jun Chen,et al.  Large‐Area Nanowire Arrays of Molybdenum and Molybdenum Oxides: Synthesis and Field Emission Properties , 2003 .

[10]  Y. Bando,et al.  Field emission from MoO3 nanobelts , 2002 .

[11]  Klaus Kern,et al.  Scanning field emission from patterned carbon nanotube films , 2000 .

[12]  N. Xu,et al.  Correlation between resistance and field emission performance of individual ZnO one-dimensional nanostructures. , 2008, ACS nano.

[13]  Kuo-Feng Chen,et al.  Field emission image uniformity improvement by laser treating carbon nanotube powders , 2006 .

[14]  Jun Chen,et al.  Field emission display device structure based on double-gate driving principle for achieving high brightness using a variety of field emission nanoemitters , 2007 .

[15]  Dmitri Golberg,et al.  Quasi‐Aligned Single‐Crystalline W18O49 Nanotubes and Nanowires , 2003 .

[16]  K. Yong,et al.  Direct synthesis of W18O49 nanorods from W2N film by thermal annealing , 2007 .