Degradation of nonencapsulated polymer-based light-emitting diodes: Noise and morphology

We show that the degradation of a nonencapsulated polymer-based light-emitting diode (LED) is accompanied by the appearance of strong fluctuations,—that is noise both in the radiance and in the film resistance. We demonstrate a correlation between the morphological changes which occur during the degradation process and the noise, suggesting that the sampling of noise during LED operation can be used as a very efficient tool to predict the approaching failure of LEDs in real-life applications. The morphological changes in LED degradation are essentially a two-stage process. First, there is formation of “bubbles” at the metal–polymer interface due to delamination of the polymer film from the metal surface. Second, carbonized areas in the form of “black spots” are formed. Accumulation of carbonized areas leads to short and/or open circuits and final LED failure.

[1]  Hany Aziz,et al.  A degradation mechanism of organic light-emitting devices , 1996 .

[2]  W. R. Salaneck,et al.  The metal‐on‐polymer interface in polymer light emitting diodes , 1996 .

[3]  B. Cumpston,et al.  In situ characterization of the oxidative degradation of a polymeric light emitting device , 1997 .

[4]  Franco Cacialli,et al.  Characterization of properties of polymeric light-emitting diodes over extended periods , 1994 .

[5]  L. Do,et al.  Morphological change in the degradation of Al electrode surfaces of electroluminescent devices by fluorescence microscopy and AFM , 1996 .

[6]  Klavs F. Jensen,et al.  Photo-oxidation of polymers used in electroluminescent devices , 1995 .

[7]  Akira J. Ikushima,et al.  Observation of degradation processes of Al electrodes in organic electroluminescence devices by electroluminescence microscopy, atomic force microscopy, scanning electron microscopy, and Auger electron spectroscopy , 1994 .

[8]  Howard W. H. Lee,et al.  Photo‐oxidation of electroluminescent polymers studied by core‐level photoabsorption spectroscopy , 1996 .

[9]  H. Antoniadis,et al.  Formation and growth of black spots in organic light‐emitting diodes , 1996 .

[10]  Marie Angelopoulos,et al.  Polymeric anodes for improved polymer light-emitting diode performance , 1997 .

[11]  K. Pichler,et al.  Conjugated polymer electroluminescence: technical aspects from basic devices to commercial products , 1997, Philosophical Transactions of the Royal Society of London. Series A: Mathematical, Physical and Engineering Sciences.

[12]  D. L. Thomsen,et al.  A chemical failure mechanism for aluminum(III) 8-hydroxyquinoline light-emitting devices , 1996 .

[13]  L. Do,et al.  Crystallization of organic thin films for electroluminescent devices , 1996 .

[14]  S. Forrest,et al.  Reliability and degradation of organic light emitting devices , 1994 .

[15]  Siegfried Karg,et al.  Increased brightness and lifetime of polymer light-emitting diodes with polyaniline anodes , 1996 .

[16]  A. I. Mikhailov,et al.  The photo-oxidation of polymers—1. Initiation of polystyrene photo-oxidation , 1993 .

[17]  J. Salbeck.  Electroluminescence with organic compounds , 1996 .

[18]  J. C. Scott,et al.  Degradation and failure of MEH‐PPV light‐emitting diodes , 1996 .