论文信息 - Interface Properties of Copper/Aluminum/Stainless Steel Clad Materials

Interface Properties of Copper/Aluminum/Stainless Steel Clad Materials

Copper/aluminum/stainless steel (Cu/Al/STS) clad materials were made by rolling and heat treatment process. These specimens were evaluated the formability and bonding strength of Cu/Al/STS clad materials. Thin disc specimens for TEM observation were prepared from the interfaces of Cu/Al and Al/STS by using the Focused Ion Beam (FIB) utility. Brittle oxide film formed on copper surface during heat treatment at 673K~773K. Diffusion bonding was observed at the interface of Cu/Al. Reacted region was formed in the interface of Al/STS with width about 10nm, while in the case of Cu/Al was formed about 1,600nm width. It was also observed nanosized crevice in reacted region of Al/STS interfaces.

[1] Soo Woo Nam,et al. The Mechanical Behavior of Materials X , 2007, Key Engineering Materials.

[2] Hyung-ki Park,et al. Fabrication of aluminum/copper clad composite using hot hydrostatic extrusion process and its material characteristics , 2004 .

[3] H. Çelik,et al. Electrical and thermal properties of the interface at diffusion-bonded and soldered 304 stainless steel and copper bimetal , 2003 .

[4] Krishnamorthy Raghukandan,et al. Analysis of the explosive cladding of cu–low carbon steel plates , 2003 .

[5] K. Sassaman,et al. Archaeology Division: 2001 AAA Program , 2001 .

[6] A. Taheri,et al. GROWTH RATE OF INTERMETALLIC COMPOUNDS IN AL/CU BIMETAL PRODUCED BY COLD ROLL WELDING PROCESS , 2001 .