Some contributions of electron fractography to the theory of fracture

A survey is given of the results of five years electron fractography as conducted at the National Aerospace Laboratory N.L.R. and of the contribution of this work to the comprehension of fatigue cracking, ductile fracture, cleavage and stress corrosion.

[1]  M. De.  Handbuch der Physik , 1957 .

[2]  J. F. Nankivell,et al.  Sources of error in electron stereomicroscopy , 1958 .

[3]  K. Puttick.  Ductile fracture in metals , 1959 .

[4]  Correction of errors in electron stereomicroscopy , 1960 .

[5]  G. Smith,et al.  Crack propagation in high stress fatigue , 1962 .

[6]  Stereoscopic viewing of metal foils in the electron microscope , 1962 .

[7]  J. F. Nankivell.  Minimum differences in height detectable in electron stereomicroscopy , 1962 .

[8]  A. Mcevily,et al.  On fatigue crack propagation in F.C.C. metals , 1963 .

[9]  P. Forsyth.  Fatigue damage and crack growth in aluminium alloys , 1963 .

[10]  J. Friedel.  CHAPTER VI – IMPERFECT DISLOCATIONS , 1964 .

[11]  C. Beachem.  Electron Fractographic Studies of Mechanical Fracture Processes in Metals , 1965 .

[12]  OBSERVATION OF CRACK PROPAGATION ON THE FRACTURE SURFACE , 1965 .

[13]  Osamu Tamate,et al.  The effect of a circular inclusion on the stresses around a line crack in a sheet under tension , 1968 .

[14]  B. J. Brindley.  The mechanism of ductile fracture in an Fe-21 %Cr-0.05 % C alloy , 1968 .

[15]  B. Tomkins,et al.  Low endurance fatigue in metals and polymers , 1969 .

[16]  E. Ruedl.  Void formation at the interface between particles and matrix in deformed Al-Al2O3 foils , 1969 .

[17]  F. Bradshaw,et al.  The influence of gaseous environment and fatigue frequency on the growth of fatigue cracks in some aluminum alloys , 1969 .

[18]  The microstructure of fatigue fracture surfaces , 1969 .

[19]  R. Wanhill.  Fractography of Stress Corrosion in Ti-8A1 Tested in Fatigue , 1970 .

[20]  J. Spretnak,et al.  A suggestion on the nature of the “Plastic stretch zone” in prefatigued plane strain fracture toughness specimens , 1970 .

[21]  D. Broek.  A critical note on electron fractography , 1970 .

[22]  Robert P. Wei,et al.  Environmental fatigue crack propagation of aluminum alloys at low stress intensity levels , 1970 .

[23]  The study of fracture surface profiles in the electron microscope , 1970 .

[24]  D. Meyn.  An analysis of frequency and amplitude effects on corrosion fatigue crack propagation in Ti-8Al-1Mo-1V , 1971 .

[25]  D. Meyn.  Cleavage in Ti-8Al-1Mo-1V caused by hydrogen gas , 1972 .

[26]  D. Broek.  Correlation between stretched zone size and fracture toughness , 1972 .

[27]  R. Wanhill.  Fractographic Interpretation of Subcritical Cracking in a High Strength Titanium Alloy (IMI 550) , 1973 .

[28]  R. Wanhill.  A consideration of cleavage in alpha titanium , 1973 .

[29]  R. Wanhill.  Formation of River Markings During Sub-Critical Cracking of Titanium and its Alloys , 1973 .

[30]  J. Schijve,et al.  The role of inclusions in fatigue crack initiation in an aluminum alloy , 1973 .