Damage Tolerance of FSWed Integral Wing Panel Reinforced by Bonded Crack Retarders

A total of 2195 T8 samples were designed, and the friction stir weld lines were kept in the sample center. Two kinds of crack retarders were designed and bonded onto the samples in three different positions. Fatigue tests were performed with and without crack retarders bonded on the samples. Crack growth rates and fatigue lives were measured and compared with each other. The effect of crack retarder’s width and position on damage tolerance was studied. Crack paths were observed and studied. It is shown that the wider size crack retarder can improve fatigue life even two times more than the narrower one, and it can make crack paths smooth. The damage tolerance of the panel achieves the best performance when the retarder covers the weld zone completely.

[1]  C. Dalle Donne,et al.  Residual stress effects on fatigue crack propagation in friction stir welds , 2001 .

[2]  Phil E. Irving,et al.  Size effects on residual stress and fatigue crack growth in friction stir welded 2195-T8 aluminium – Part I: Experiments , 2011 .

[3]  K. Sadananda,et al.  Residual stress effects on near-threshold fatigue crack growth in friction stir welds in aerospace alloys , 2003 .

[4]  Giuliano Allegri,et al.  Design and Modeling of Selective Reinforcements for Integral Aircraft Structures , 2007 .

[5]  Anthony P. Reynolds,et al.  Residual Stress and Microstructure Effects on Fatigue Crack Growth in AA2050 Friction Stir Welds , 2008 .

[6]  L. Edwards,et al.  Evolution of residual stresses with fatigue crack growth in integral structures with crack retarders , 2016 .

[7]  G. Biallas,et al.  Role of Residual Stresses on Fatigue Crack Propagation of FSW 6056-T78 Aluminium Joints under Various Technologies , 2006 .

[8]  Livan Fratini,et al.  Fatigue Crack Growth in 2024-T351 Friction Stir Welded Joints: Longitudinal Residual Stress and Microstructural Effects , 2009 .

[9]  Michael A. Sutton,et al.  A Study of Residual Stresses and Microstructure in 2024-T3 Aluminum Friction Stir Butt Welds , 2002 .

[10]  Phil E. Irving,et al.  The role of residual stress and heat affected zone properties on fatigue crack propagation in friction stir welded 2024-T351 aluminium joints , 2003 .

[11]  Giuliano Allegri,et al.  Fail-safe design of integral metallic aircraft structures reinforced by bonded crack retarders , 2009 .

[12]  Yazhi Li,et al.  Damage Tolerance and Fail Safety of Welded Aircraft Wing Panels , 2005 .

[13]  J. Schijve,et al.  Crack stoppers and ARALL laminates , 1989 .

[14]  C. Dalle Donne,et al.  Effects of Weld Imperfections and Residual Stresses on the Fatigue Crack Propagation in Friction Stir Welded Joints , 2000 .

[15]  Sangshik Kim,et al.  Fatigue crack propagation behavior of friction stir welded Al–Mg–Si alloy , 2006 .

[16]  Distortion and residual stresses in structures reinforced with titanium straps for improved damage tolerance , 2008 .