Prediction of cover crack propagation in RC structures caused by corrosion

The paper proposes a model relating the level of reinforcement corrosion (in terms of loss of rebar radius) with the width of corrosion-induced cracks. The model is developed using a simulation of the process of corrosion-induced crack opening by means of finite-element (FE) modelling. Concrete is treated as a linear elastic material, a vertical crack is introduced above a reinforcing bar and expansive behaviour of corrosion products is modelled using a thermal analogy. Corrosion products are divided into those that penetrate (dissipate) into cracks (no crack propagation) and those that cause crack opening. The amount of corrosion products penetrating into cracks at a specified crack width is evaluated using FE modelling and analyses of experimental results. It was found that a corrosion loss of 0·1–0·4 mm dissipated into the cracks when the crack width was 1·0 mm. The influence of geometric parameters such as rebar diameter, spacing and location, and thickness of top and edge concrete covers were investi...

[1]  Palle Thoft-Christensen.  Service Life Definitions based on Corrosion Crack Width , 2005 .

[2]  Mark G. Stewart,et al.  Corrosion-Induced Cracking: Experimental Data and Predictive Models , 2005 .

[3]  J. Rodriguez,et al.  Corrosion of Reinforcement and Service Life of Concrete Structures , 1996 .

[4]  Sudhir Misra,et al.  Corrosion products of reinforcing bars embedded in concrete , 1993 .

[5]  J. G. Cabrera,et al.  Deterioration of concrete due to reinforcement steel corrosion , 1996 .

[6]  V. Saouma,et al.  Numerical Simulation of Reinforced Concrete Deterioration: Part 2—Steel Corrosion and Concrete Cracking , 1999 .

[7]  A. Hillerborg,et al.  Analysis of crack formation and crack growth in concrete by means of fracture mechanics and finite elements , 1976 .

[8]  S. Kulendran,et al.  Finite Element Modeling of Corrosion Damage in Concrete Structures , 1992 .

[9]  Khaled Soudki,et al.  Effectiveness of Impressed Current Technique to Simulate Corrosion of Steel Reinforcement in Concrete , 2003 .

[10]  Cruz Alonso,et al.  Cover cracking as a function of rebar corrosion: Part 2—Numerical model , 1993 .

[11]  M. S. Elgarf,et al.  Bond characteristics of corrding reinforcement in concrete beams , 1999 .

[12]  Dimitri V. Val,et al.  Prediction of corrosion-induced cover cracking in reinforced concrete structures , 2011 .

[13]  Robert E. Melchers,et al.  Analytical Model for Corrosion-Induced Crack Width in Reinforced Concrete Structures , 2006 .

[14]  Mark G. Stewart,et al.  Stochastic Assessment of Timing and Efficiency of Maintenance for Corroding RC Structures , 2009 .

[15]  Byung Hwan Oh,et al.  Effects of non-uniform corrosion on the cracking and service life of reinforced concrete structures , 2010 .

[16]  Palle Thoft-Christensen,et al.  Numerical study of corrosion crack opening , 2008 .

[17]  Mark G. Stewart,et al.  Corrosion-Induced Cover Cracking: New Test Data and Predictive Models , 2011 .

[18]  Dimitri V. Val.  Factors Affecting Life-Cycle Cost Analysis of RC Structures in Chloride Contaminated Environments , 2007 .

[19]  C. Andrade,et al.  Factors controlling cracking of concrete affected by reinforcement corrosion , 1998 .

[20]  Dimitri V. Val,et al.  Analytical modelling of concrete cover cracking caused by corrosion of reinforcement , 2010 .

[21]  Thierry Vidal,et al.  ANALYZING CRACK WIDTH TO PREDICT CORROSION IN REINFORCED CONCRETE , 2004 .

[22]  Koichi Maekawa,et al.  Simulation of Coupled Corrosive Product Formation, Migration into Crack and Propagation in Reinforced Concrete Sections , 2005 .

[23]  W. Jin,et al.  On the penetration of corrosion products from reinforcing steel into concrete due to chloride-induced corrosion , 2010 .

[24]  Palle Thoft-Christensen.  What Happens with Reinforced Concrete Structures when the Reinforcement Corrodes , 2001 .

[25]  Dimitri V. Val,et al.  Reliability Assessment of Ageing Reinforced Concrete Structures—Current Situation and Future Challenges , 2009 .

[26]  Y. Li,et al.  Spatial variability of concrete deterioration and repair strategies , 2004 .

[27]  Cruz Alonso,et al.  Cover cracking as a function of bar corrosion: Part I-Experimental test , 1993 .

[28]  Dimitri V. Val,et al.  Experimental and Numerical Investigation of Corrosion-Induced Cover Cracking in Reinforced Concrete Structures , 2009 .

[29]  A. Castel,et al.  Concrete cover cracking with reinforcement corrosion of RC beam during chloride-induced corrosion process , 2010 .

[30]  K. Lundgren,et al.  Modelling the effect of corrosion on bond in reinforced concrete , 2002 .