Triaxial test results for fibre-reinforced composites: The Second World-Wide Failure Exercise benchmark data

This article describes a unique set of experimental results employed in benchmarking leading three-dimensional failure criteria, as a part of the Second World Wide Failure Exercise (WWFE-II). In Part A of WWFE-II, the originators of those criteria (or their representative) made blind theoretical predictions of the triaxial strength, stress–strain curves and deformation of 12 Test Cases, selected by the organisers to challenge the contributors’ models. The cases covered various materials and laminates subjected to a wide range of triaxial and through-thickness loading conditions. The Test Cases were for (a) an isotropic material made of an epoxy polymer, (b) various 0° unidirectional laminae and (c) (0°/90°)s, (0°/±45°/90°)s and (±35°)s multi-directional laminates. In Part B of WWFE-II, a comparison is made by the contributors between available experimental results, described here, and their theoretical predictions, made in Part A. Discussion is also made on the accuracy of these results.

[1]  Donald F. Adams,et al.  In-plane and interlaminar Iosipescu shear properties of various graphite fabric/epoxy laminates , 1987 .

[2]  A. Wronski,et al.  Compressive failure and kinking in uniaxially aligned glass-resin composite under superposed hydrostatic pressure , 1982 .

[3]  S. Swanson,et al.  Ranking of laminates for edge delamination resistance , 1994 .

[4]  A. Wronski,et al.  Axial compressive failure of glass-fibre polyester composites under superposed hydrostatic pressure: influence of fibre bundle size , 1992 .

[5]  P. Krawczak,et al.  Fracture Mechanics Applied to Glass Fibre/Epoxy Matrix Interface Characterization , 1995 .

[6]  S. Swanson,et al.  Mechanical characterization of IM7/8551-7 carbon/epoxy under biaxial stress: (Final report) , 1987 .

[7]  K. L. Gipple,et al.  Measurement of the Out-of-Plane Shear Response of Thick Section Composite Materials Using the V-Notched Beam Specimen , 1994 .

[8]  John E. Deibler,et al.  Mode I and Mixed Mode Energy Release Rate Values for Delamination of Graphite/Epoxy Test Specimens , 1987 .

[9]  Constantinos Soutis,et al.  Measuring the notched compressive strength of composite laminates : Specimen size effects , 2008 .

[10]  P. D. Soden,et al.  Influence of winding angle on the strength and deformation of filament-wound composite tubes subjected to uniaxial and biaxial loads , 1993 .

[11]  Characterization of Aerospace Grade Resins and Composites Through Pressurized Volumetric Dilatometry , 1992 .

[12]  I. Daniel,et al.  Rate Effects on Delamination Fracture Toughness of Graphite/Epoxy Composites , 1987 .

[13]  Stephen W. Tsai,et al.  Three-Dimensional Effective Moduli of Orthotropic and Symmetric Laminates , 1992 .

[14]  D. C. Freeman,et al.  The Effects of Through-thickness Compression on the Interlaminar Shear Response of Laminated Fiber Composites , 2004 .

[15]  A. Wronski,et al.  Pyramidal yield criteria for epoxides , 1977 .

[16]  J. Webber,et al.  Non-linear stress-strain behaviour of carbon fibre reinforced plastic laminates , 1981 .

[17]  Kyong Yop Rhee,et al.  Effects of Hydrostatic Pressure on the Compressive Properties of Laminated, 0° Unidirectional, Graphite Fiber/Epoxy Matrix Thick-Composite , 1995 .

[18]  M. Hinton,et al.  Determining the through-thickness properties of FRP materials , 1998 .

[19]  S. Swanson,et al.  Characterization of Prepreg Tow Carbon/Epoxy Laminates , 1989 .

[20]  R. Tennyson,et al.  Closure of the Cubic Tensor Polynomial Failure Surface , 1989 .

[21]  Mechanical properties of unidirectional organic-fiber-reinforced plastics under hydrostatic pressure , 1998 .

[22]  M. J. Messick,et al.  Failure of Carbon/Epoxy Lamina Under Combined Stress , 1987 .

[23]  Y. Huang,et al.  Measurement of the fracture toughness of a fiber-reinforced composite using the Brazilian disk geometry , 1997 .

[24]  M. Wisnom,et al.  Size effects in unnotched tensile strength of unidirectional and quasi-isotropic carbon/epoxy composites , 2008 .

[25]  R. Caddell,et al.  Influence of hydrostatic pressure on the yield strength of anisotropic polycarbonate , 1981 .

[26]  M. Hinton.  Failure Criteria in Fibre-Reinforced-Polymer Composites: The World-Wide Failure Exercise , 2004 .

[27]  Kyong Yop Rhee,et al.  Effects of hydrostatic pressure on the compressive behavior of thick laminated 45 ° and 90 ° unidirectional graphite-fiber/epoxy-matrix composites , 1995 .

[28]  J. Lankford.  The effect of hydrostatic pressure and loading rate on compressive failure of fiber-reinforced ceramic-matrix composites , 1994 .

[29]  C. P. Hoppel,et al.  Literature Review-Effects of Hydrostatic Pressure on the Mechanical Behavior of Composite Materials , 1995 .

[30]  Constantinos Soutis,et al.  A study on the compressive strength of thick carbon fibre-epoxy laminates , 2007 .

[31]  A. Wronski,et al.  Kinking and compressive failure in uniaxially aligned carbon fibre composite tested under superposed hydrostatic pressure , 1982 .

[32]  N. Fleck,et al.  The failure of composite tubes due to combined compression and torsion , 1994 .

[33]  Yi Zhao.  TORQUE LIMIT FOR BOLTED JOINT FOR COMPOSITES PART A TTTC PROPERTIES OF LAMINATED COMPOSITES , 2003 .

[34]  Ronald Krueger,et al.  IMPLEMENTATION OF INTERLAMINAR FRACTURE MECHANICS IN DESIGN: AN OVERVIEW , 2003 .

[35]  P. Soden,et al.  Theoretical through-thickness elastic constants for filament-wound tubes , 1994 .

[36]  As Kaddour,et al.  Maturity of 3D failure criteria for fibre-reinforced composites: Comparison between theories and experiments: Part B of WWFE-II , 2013 .

[37]  Tensile failure of pultruded glass-polyester composites under superimposed hydrostatic pressure , 1991 .

[38]  K. Pae,et al.  The Effects of Hydrostatic Pressure on the Mechanical Behavior of Polymers , 1975 .

[39]  H. Couque,et al.  Failure mechanisms in a unidirectional fibre-reinforced thermoplastic composite under uniaxial, in-plane biaxial and hydrostatically confined compression , 1993 .

[40]  R. S. Raghava,et al.  Pressure dependent yield criteria for polymers , 1974 .

[41]  P. Soden,et al.  Design of a High Pressure Rig for Biaxial and Triaxial Compression Testing of Composite Tubes , 1996 .

[42]  John J. Lewandowski,et al.  Effects of hydrostatic pressure on mechanical behaviour and deformation processing of materials , 1998 .

[43]  MJ Hinton,et al.  The background to the Second World-Wide Failure Exercise , 2012 .

[44]  S. R. Swanson,et al.  Comparison of torsion tube and Iosipescu in-plane shear test results for a carbon fibre-reinforced epoxy composite , 1985 .

[45]  A. Miyase.  Transverse tensile strength anisotropy in thick filament wound ring composites , 1984 .

[46]  K. Pae.  The macroscopic yielding behaviour of polymers in multiaxial stress fields , 1977 .

[47]  P. D. Soden,et al.  Lamina properties, lay-up configurations and loading conditions for a range of fibre-reinforced composite laminates , 1998 .

[48]  J. Reeder.  Stitching vs. a Toughened Matrix: Compression Strength Effects , 1995 .

[49]  K. Pae,et al.  The Influence of Pressure on the Mechanical Behavior of Polychlorotrifluoroethylene , 1972 .

[50]  P. D. Soden,et al.  Biaxial test results for strength and deformation of a range of E-glass and carbon fibre reinforced composite laminates: failure exercise benchmark data , 2002 .

[51]  A. Wronski,et al.  Transverse tensile strength of glass/polyester unidirectionally aligned composites determined in diametral compression , 1990 .

[52]  K. Pae,et al.  Effects of Hydrostatic Pressure on the Torsional Shear Behavior of Graphite/Epoxy Composites , 1992 .

[53]  A. Wronski,et al.  The effect of hydrostatic pressure on transverse strength of glass and carbon fibre-epoxy composites , 1990 .

[54]  J. G. Williams,et al.  Deformation of a carbon-epoxy composite under hydrostatic pressure , 1975 .

[55]  K. Pae,et al.  Effects of Hydrostatic Pressure on In-Plane Shear Properties of Graphite/Epoxy Composites , 1992 .

[56]  Ozden O. Ochoa,et al.  Transverse and Longitudinal CTE Measurements of Carbon Fibers and their Impact on Interfacial Residual Stresses in Composites , 2006 .

[57]  K. Pae.  Influence of hydrostatic pressure on the mechanical behavior and properties of unidirectional, laminated, graphite-fiber/epoxy-matrix thick composites , 1996 .

[58]  A. Wronski,et al.  Kinking and tensile, compressive and interlaminar shear failure in carbon-fibre-reinforced plastic beams tested in flexure , 1981 .

[59]  A. Wronski,et al.  The effect of hydrostatic pressure on the tensile properties of pultruded CFRP , 1985 .

[60]  K. Pae,et al.  Effects of Hydrostatic Pressure on the Mechanical Behavior of Polymers: Polyurethane, Polyoxymethylene, and Branched Polyethylene , 1974 .

[61]  As Kaddour,et al.  Input data for test cases used in benchmarking triaxial failure theories of composites , 2012 .

[62]  As Kaddour,et al.  The effect of hydrostatic pressure on the mechanical properties of glass fibre/epoxy unidirectional composites , 2005 .

[63]  P. D. Soden,et al.  Failure of ±55 Degree Filament Wound Glass/Epoxy Composite Tubes under Biaxial Compression , 1998 .

[64]  P. D. Soden,et al.  Design of end plugs and specimen reinforcement for testing ±55° glass/epoxy composite tubes under biaxial compression , 2005 .

[65]  Ludo Van Schepdael,et al.  The behavior of high-strength unidirectional composites under tension with superposed hydrostatic pressure , 2001 .