Analysis of AISI 1020 steel corrosion in seawater by coupling electrochemical noise and optical microscopy

Abstract Electrochemical noise coupled to in situ optical micrographs was used to study corrosion processes in AISI 1020 steel immersed in seawater. The noise data was analysed using wavelet transform. The results were represented in energy diagrams and showed that considerable changes occurred in the corrosion mechanism during the initial step of the experiment (until 7200 s). During this initial step, it was observed that the corrosion was predominantly localized by means of pitting formation and intergranular corrosion. After approximately 50,000 s (14 h) of immersion, general corrosion processes become dominant. The conclusions obtained from the analysis of the current noise signal using the wavelet transform were confirmed by optical micrograph which suggests that the coupling of electrochemical noise and optical microscopy techniques can be valuable in studying corrosion processes in this system. Another advantage of this procedure is the elucidation and separation of corrosion processes, such as, for example, pitting and intergranular ones, that are not commonly identified by other techniques.

[1]  Nestor Perez,et al.  Electrochemistry and Corrosion Science , 2004 .

[2]  P. Marcus,et al.  Localized corrosion (pitting): A model of passivity breakdown including the role of the oxide layer nanostructure , 2008 .

[3]  S. K. Sadrnezhaad,et al.  Electrochemical potential noise analysis of Cu–BTA system using wavelet transformation , 2009 .

[4]  Odemir Martinez Bruno,et al.  Investigation of AISI 1040 steel corrosion in H2S solution containing chloride ions by digital image processing coupled with electrochemical techniques , 2011 .

[5]  R. Cottis,et al.  A practical evaluation of electrochemical noise parameters as indicators of corrosion type , 2004 .

[6]  Jong Jip Kim.  Wavelet analysis of potentiostatic electrochemical noise , 2007 .

[7]  Tomomi Murata,et al.  A spectrum analysis of potential fluctuation during passive film breakdown and repair on iron , 1992 .

[8]  G. Bell,et al.  Detection of stress corrosion cracking and general corrosion of mild steel in simulated defense nuclear waste solutions using electrochemical noise analysis , 1997 .

[9]  Janusz Smulko,et al.  Detection of random transients caused by pitting corrosion , 2002 .

[10]  M. Amin,et al.  AC and DC studies of the pitting corrosion of Al in perchlorate solutions , 2006 .

[11]  Y. F. Cheng,et al.  The role of chloride ions in pitting of carbon steel studied by the statistical analysis of electrochemical noise , 1999 .

[12]  Changjian Lin,et al.  Study on the corrosion behavior of reinforcing steel in cement mortar by electrochemical noise measurements , 2007 .

[13]  E. García-Ochoa,et al.  Assessment of the dynamics of corrosion fatigue crack initiation applying recurrence plots to the analysis of electrochemical noise data , 2008 .

[14]  Changjian Lin,et al.  A study on the initiation of pitting corrosion in carbon steel in chloride-containing media using scanning electrochemical probes , 2010 .

[15]  Y. F. Cheng,et al.  Spectral analysis of electrochemical noise with different transient shapes , 2000 .

[16]  F. Cao,et al.  Electrochemical noise analysis of LY12-T3 in EXCO solution by discrete wavelet transform technique , 2006 .

[17]  Janusz Smulko,et al.  Pitting corrosion characterization by electrochemical noise measurements on asymmetric electrodes , 2009 .

[18]  J. L. Hudson,et al.  A spatiotemporal model of interactions among metastable pits and the transition to pitting corrosion , 2005 .

[19]  N. Parvathavarthini,et al.  Assessment of intergranular corrosion (IGC) in 316(N) stainless steel using electrochemical noise (EN) technique , 2009 .

[20]  Shenhao Chen,et al.  In situ characterization of localized corrosion of stainless steel by scanning electrochemical microscope , 2009 .

[21]  Peter Planinsic,et al.  Characterization of corrosion processes by current noise wavelet-based fractal and correlation analysis , 2008 .

[22]  Manuel Bethencourt,et al.  Using wavelets transform in the analysis of electrochemical noise data , 1999 .

[23]  G. Song,et al.  Electrochemical potential noise of 321 stainless steel stressed under constant strain rate testing conditions , 2007 .

[24]  G. Frankel.  Pitting Corrosion of Metals A Review of the Critical Factors , 1998 .

[25]  Changjian Lin,et al.  Corrosion initiation of stainless steel in HCl solution studied using electrochemical noise and in-situ atomic force microscope , 2009 .

[26]  A S Mikhailov,et al.  Sudden Onset of Pitting Corrosion on Stainless Steel as a Critical Phenomenon , 2004, Science.

[27]  Ying Li,et al.  Pitting mechanism on an austenite stainless steel nanocrystalline coating investigated by electrochemical noise and in-situ AFM analysis , 2008 .

[28]  D. Macdonald,et al.  Stress corrosion cracking of sensitized Type 304 stainless steel in thiosulphate solution. II. Dynamics of fracture , 2006 .

[29]  J. L. Hudson,et al.  Detection of Interactions among Localized Pitting Sites on Stainless Steel Using Spatial Statistics , 2005 .

[30]  H. S. Khatak,et al.  Determination of corrosion types for AISI type 304L stainless steel using electrochemical noise method , 2005 .

[31]  Jinping Ou,et al.  Corrosion monitoring of reinforcing steel in cement mortar by EIS and ENA , 2007 .

[32]  John R. Scully,et al.  Electrochemical noise measurement for corrosion applications , 1996 .

[33]  Wei Shi,et al.  Initiation and repassivation of pitting corrosion of carbon steel in carbonated concrete pore solution , 2011 .

[34]  Tiedo Tinga,et al.  Time–frequency methods for trend removal in electrochemical noise data , 2012 .

[35]  A. Legat,et al.  Chaotic Analysis of Electrochemical Noise Measured on Stainless Steel , 1995 .