Effect of substrate temperature on poly(methyl methacrylate) nanocomposite thin films deposited by matrix assisted pulsed laser evaporation

Abstract The effects of substrate heating on thin films deposited by matrix assisted pulsed laser evaporation (MAPLE) were investigated. Substrates were heated at temperatures ranging from 315 to 425 K during depositions of neat poly(methyl methacrylate) (PMMA) and PMMA–carbon nanotube (CNT) composite thin films. Scanning electron microscopy (SEM) was used to examine the surface morphology of deposited films, while gel permeation chromatography (GPC) was used to determine the extent of photon-induced degradation in the molecular weight of deposited polymer. Significant reductions in molecular weight were observed. Further information regarding the degradation behavior was obtained from differential scanning calorimetry (DSC), where the glass transition temperatures (Tg) of native and MAPLE deposited PMMA samples were measured. A decrease in the surface roughness of deposited films was observed with increasing substrate temperature for both neat PMMA and PMMA–CNT composite films. At temperatures significantly lower than the measured Tg for the as-received PMMA, features in deposited films began to take on a disc-like structure. DSC analysis of the deposited species shows a decrease in Tg relative to the as-received material. This reduction in Tg is attributed to the degradation of the native polymer during the MAPLE process, as shown by GPC results. Surface roughness effects in both the neat polymer and composite films show a continuous decrease in roughness as a function of temperature, as observed by both profilometry and SEM. The final roughnesses of the composite films were significantly greater than those of the pure polymer films. It is speculated that this is the result of CNT agglomeration within the starting target solutions.

[1]  K. Dalnoki-Veress,et al.  Molecular weight dependence of reductions in the glass transition temperature of thin, freely standing polymer films. , 2001, Physical review. E, Statistical, nonlinear, and soft matter physics.

[2]  Tatiana Itina,et al.  Matrix-assisted pulsed laser evaporation of polymeric materials: a molecular dynamics study , 2001 .

[3]  R. A. McGill,et al.  Matrix-assisted laser deposition of a sorbent oligomer using an infrared laser , 2004 .

[4]  S. Bourbigot,et al.  Preparation of Homogeneously Dispersed Multiwalled Carbon Nanotube/Polystyrene Nanocomposites via Melt Extrusion Using Trialkyl Imidazolium Compatibilizer , 2005 .

[5]  S. Simon,et al.  Polystyrene freeze-dried from dilute solution : Tg depression and residual solvent effects , 2006 .

[6]  Uzodinma Okoroanyanwu,et al.  Thin film instabilities and implications for ultrathin resist processes , 2000 .

[7]  S. Roth,et al.  Electrical and mechanical properties of nanocomposites of single wall carbon nanotubes with PMMA , 2005 .

[8]  Thomas Lippert,et al.  Chemical and spectroscopic aspects of polymer ablation: special features and novel directions. , 2003, Chemical reviews.

[9]  Clifford L. Henderson,et al.  Influence of molecular weight and film thickness on the glass transition temperature and coefficient of thermal expansion of supported ultrathin polymer films , 2004 .

[10]  D. Froelich,et al.  Glass transition temperature of ideal polymeric networks , 1976 .

[11]  M. Vrnata,et al.  Thin organic layers prepared by MAPLE for gas sensor application , 2006, 2006 Conference on Optoelectronic and Microelectronic Materials and Devices.

[12]  L. Zhigilei,et al.  Laser processing of polymer nanocomposite thin films , 2006 .

[13]  J. M. Fitz-Gerald,et al.  Pulsed laser deposition vs. matrix assisted pulsed laser evaporation for growth of biodegradable polymer thin films , 2005 .

[14]  J. Schou,et al.  Surface morphology of polyethylene glycol films produced by matrix-assisted pulsed laser evaporation (MAPLE): Dependence on substrate temperature , 2006 .

[15]  Vijay K. Varadan,et al.  Carbon nanotube/PMMA composite thin films for gas-sensing applications , 2003 .

[16]  Joseph L. Keddie,et al.  Interface and surface effects on the glass-transition temperature in thin polymer films , 1994 .

[17]  I. Stamatin,et al.  Pulsed laser deposition of biocompatible polymers: a comparative study in case of pullulan , 2004 .

[18]  K. Ute,et al.  Glass transition temperature and melting temperature of uniform isotactic and syndiotactic poly(methyl methacrylate)s from 13mer to 50mer , 1995 .

[19]  B. Dong,et al.  A study on carbon nanotubes reinforced poly(methyl methacrylate) nanocomposites , 2005 .

[20]  James A. Forrest,et al.  Interface and chain confinement effects on the glass transition temperature of thin polymer films , 1997 .

[21]  J. Schou,et al.  High laser-fluence deposition of organic materials in water ice matrices by “MAPLE” , 2005 .

[22]  Yiu-Wing Mai,et al.  Dispersion and alignment of carbon nanotubes in polymer matrix: A review , 2005 .

[23]  S. Park,et al.  Synthesis and Dispersion Characteristics of Multi‐Walled Carbon Nanotube Composites with Poly(methyl methacrylate) Prepared by In‐Situ Bulk Polymerization , 2003 .

[24]  T. Kashiwagi,et al.  Flammability properties of polymer nanocomposites with single-walled carbon nanotubes: effects of nanotube dispersion and concentration * , 2005 .

[25]  L. Zhigilei,et al.  Making molecular balloons in laser-induced explosive boiling of polymer solutions. , 2007, Physical review letters.