Self-healing ability of fly ash–cement systems

Abstract Concrete is susceptible to cracking due to both autogenous and drying shrinkage. Nevertheless, most of these types of cracks occur before 28 days. Because fly ash continues to hydrate after 28 days, it is likely that hydrated products from fly ash may modify microstructure, seal these cracks, and prolong the service life. This research investigates the self-healing ability of fly ash–cement paste. Compressive strength, porosity, chloride diffusion coefficients, hydration reactions and hydrated products were studied. The research focuses on behavior after 28 days. According to the experimental results, the fly ash–cement system has the self-healing ability for cracks that occur from shrinkage. The self-healing ability increased when the fraction of fly ash increased.

[1]  Stefan Jacobsen,et al.  Self healing of high strength concrete after deterioration by freeze/thaw , 1996 .

[2]  D. Bentz,et al.  Shrinkage-reducing admixtures and early-age desiccation in cement pastes and mortars , 2001 .

[3]  T. Nawa,et al.  Effect of water curing conditions on the hydration degree and compressive strengths of fly ash–cement paste , 2006 .

[4]  Toyoharu Nawa,et al.  Effect of fly ash on autogenous shrinkage , 2005 .

[5]  H. Reinhardt,et al.  Permeability and self-healing of cracked concrete as a function of temperature and crack width , 2003 .

[6]  T. Powers,et al.  Absorption of Water by Portland Cement Paste during the Hardening Process , 1935 .

[7]  Adam Neville,et al.  Autogenous Healing—A Concrete Miracle? , 2002 .

[8]  F. H. Wittmann,et al.  On the action of capillary pressure in fresh concrete , 1976 .

[9]  Gilles Pijaudier-Cabot,et al.  Experimental characterization of the self-healing of cracks in an ultra high performance cementitious material: Mechanical tests and acoustic emission analysis , 2007 .

[10]  R. Troli,et al.  Effects of shrinkage reducing admixture in shrinkage compensating concrete under non-wet curing conditions , 2005 .

[11]  Erika Holt,et al.  Cracking risks associated with early age shrinkage , 2004 .

[12]  Carola Edvardsen,et al.  Water Permeability and Autogenous Healing of Cracks in Concrete , 1999 .

[13]  B.I.G. Barr,et al.  Shrinkage of concrete stored in natural environments , 2003 .

[14]  J. C. Taylor,et al.  Computer Programs for Standardless Quantitative Analysis of Minerals Using the Full Powder Diffraction Profile , 1991, Powder Diffraction.

[15]  B. Rongbing,et al.  Synthesis and evaluation of shrinkage-reducing admixture for cementitious materials , 2005 .