Influence of Li Additions on the Microstructure and Corrosion Response of 2XXX Series Aluminium Alloys

This paper discusses two Al-Cu alloys for aerospace applications, one of which has an addition of between 1.6 and 2.0 wt.% of Li. The alloys are AA2024-T3 (Al-Cu) and AA2099-T8E77 (Al-Cu-Li). Microstructural analysis via Field Emission Gun Transmission Electron Microscope (FEGTEM) and Field Emission Gun Scanning Electron Microscope (FEGSEM) utilising Energy Dispersive Spectroscopy (EDS) and Electron Backscatter Detector (EBSD) techniques have been used to characterise the two microstructures and phases contained within them. Anodic polarisation and immersion testing in a 3.5 wt.% NaCl solution have been carried out and a comparison of the corrosion mechanisms has been made. AA2024-T3 had a fine, equiaxed grain structure, whereas AA2099-T8E77 had a substantial amount of recrystallized grains. Finer grains were also observed on AA2099-T8E77, however, the vast majority were larger than the maximum detection limit of the EBSD technique. Intergranular and pitting corrosion were observed on both alloys following immersion testing, however, the intergranular corrosion (IGC) was more prominent on AA2099-T8E77. Anodic polarisation indicated that AA2024-T3 was more noble, highlighting that the Li-containing AA2099-T8E77 alloy was more susceptible to corrosion. The T1 (Al2CuLi) phase within AA2099-T8E77 was seen to be highly active following immersion and anodic polarisation tests. The corrosion pits on AA2099-T8E77 were seen to propagate to a depth of ~ 80 to 100 μm, with a maximum of 126 μm recorded. For AA2024-T3 the maximum depth recorded was 77 μm and the average depth was between 60 and 70 μm.

[1]  Diana Bohm.  Light Alloys Metallurgy Of The Light Metals , 2016 .

[2]  C. Henon,et al.  Comparison of Corrosion Performance and Mechanisms of Al-Cu Alloys with and without Li Addition , 2012 .

[3]  G. Thompson,et al.  Distribution of intermetallics in an AA 2099-T8 aluminium alloy extrusion , 2011 .

[4]  Wen-jing Chen,et al.  Corrosion mechanism associated with T1 and T2 precipitates of Al–Cu–Li alloys in NaCl solution , 2008 .

[5]  S. Adhikari,et al.  Factors controlling the time evolution of the corrosion potential of aluminum in alkaline solutions , 2008 .

[6]  Hosni M. Ezuber,et al.  A study on the corrosion behavior of aluminum alloys in seawater , 2008 .

[7]  J. E. O. Mayne,et al.  Corrosion of Aluminium , 2007 .

[8]  C. Giummarra,et al.  NEW ALUMINUM LITHIUM ALLOYS FOR AEROSPACE APPLICATIONS , 2007 .

[9]  李劲风,et al.  Localized corrosion mechanism associated with precipitates containing Mg in Al alloys , 2007 .

[10]  Jin-feng Li,et al.  Simulation on function mechanism of T1(Al2CuLi) precipitate in localized corrosion of Al-Cu-Li alloys , 2006 .

[11]  Jin-feng Li,et al.  Corrosion behavior of 2195 and 1420 Al-Li alloys in neutral 3.5% NaCl solution under tensile stress , 2006 .

[12]  Rudolph G. Buchheit,et al.  Electrochemical Characteristics of Intermetallic Phases in Aluminum Alloys An Experimental Survey and Discussion , 2005 .

[13]  C. Vargel.  Chapter B.2 – Types of Corrosion on Aluminium , 2004 .

[14]  Ian J. Polmear,et al.  Aluminium Alloys - A Century of Age Hardening , 2004 .

[15]  Z. Szklarska‐Śmiałowska.  Pitting corrosion of aluminum , 1999 .

[16]  M. Loretto,et al.  Influence of lithium additions on precipitation and age hardening of 7075 alloy , 1993 .

[17]  H. Flower.  Light alloys: metallurgy of the light metals , 1992 .

[18]  P. Niskanen,et al.  Corrosion of aluminum alloys containing lithium , 1982 .