On fatigue crack paths

Abstract The main features of the path taken by a propagating fatigue crack are discussed. It is assumed that a material is homogeneous and isotropic on a macroscopic scale, that behaviour is essentially elastic, and that the initial crack is ‘long’. Under these conditions the path taken by a propagating fatigue crack is reasonably well understood in a qualitative sense. There is a strong tendency for crack propagation to be in Mode I; the main exception is the slant crack propagation sometimes observed in thin sheets. A crack path is influenced by the precise characteristics of the crack tip plastic zone, by microstructural irregularities, and by the line tension of the crack front. The application of chaos theory to crack paths is explored briefly, and it is found that the concept of attractor helps in qualitative descriptions.

[1]  K. B. Broberg,et al.  On crack paths , 1987 .

[2]  Kenneth Falconer,et al.  Fractal Geometry: Mathematical Foundations and Applications , 1990 .

[3]  J. Field.  Fracture of Solids , 1964 .

[4]  H. Saunders,et al.  The Role of Crack Growth in Metal Fatigue , 1983 .

[5]  Asher A. Rubinstein,et al.  Mechanics of the crack path formation , 1991 .

[6]  Peter Joseph Edward Forsyth,et al.  The physical basis of metal fatigue , 1969 .

[7]  S. K. Maiti,et al.  Comparison of the criteria for mixed mode brittle fracture based on the preinstability stress-strain field Part I: Slit and elliptical cracks under uniaxial tensile loading , 1983 .

[8]  L. P. Pook.  On slant (45°) crack growth in fatigue , 1976 .

[9]  J. Rice,et al.  Slightly curved or kinked cracks , 1980 .

[10]  S. Nemat-Nasser,et al.  On crack path stability in a finite body , 1985 .

[11]  A. Cottrell.  Theory of crystal dislocations , 1964 .

[12]  Lekan Olaosebikan.  On the variation of stress along the front of cracks and surface flaws , 1990 .

[13]  C. Smith,et al.  Measurement of dominant eigenvalues in cracked body problems , 1989 .

[14]  L. P. Pook,et al.  Some implications of corner point singularities , 1994 .

[15]  M. W. Brown,et al.  A REVIEW OF FATIGUE CRACK GROWTH IN STEELS UNDER MIXED MODE I AND II LOADING , 1992 .

[16]  M. A. Mahmoud,et al.  Surface fatigue crack growth under combined tension and bending loading , 1990 .

[17]  D. Hull.  Tilting cracks: the evolution of fracture surface topology in brittle solids , 1993 .

[18]  Z. Bažant,et al.  Surface singularity and crack propagation , 1979 .

[19]  A. J. Ayer,et al.  The Problem of Knowledge. , 1956 .

[20]  K. Kussmaul,et al.  Fatigue under biaxial and multiaxial loading , 1991 .

[21]  Mixed mode fatigue crack growth with a sudden change in loading direction , 1993 .

[22]  Alan Cottrell,et al.  Mechanical Properties of Matter , 1964 .

[23]  Solveig Melin,et al.  Directional stability of an originally straight crack , 1992, International Journal of Fracture.

[24]  Nina Hall,et al.  The new scientist guide to chaos , 1991 .

[25]  R. Salganik,et al.  Brittle fracture of solids with arbitrary cracks , 1974 .

[26]  S. Melin.  Why do cracks avoid each other? , 1983 .

[27]  J. Schijve.  Shear lips on fatigue fractures in aluminium alloy sheet material , 1979 .

[28]  Kunigal N. Shivakumar,et al.  Treatment of singularities in cracked bodies , 1990 .

[29]  J. Benthem.  The quarter-infinite crack in a half space; Alternative and additional solutions , 1980 .

[30]  A model for predicting slant fatigue crack growth in A1 2024 , 1989 .

[31]  S. Suresh.  Fatigue of materials , 1991 .

[32]  S. Havlin,et al.  Fractals and Disordered Systems , 1991 .

[33]  J C Newman,et al.  Surface Crack Growth: Models, Experiments, and Structures , 1990 .