Impact of NaCl Contamination and Climatic Conditions on the Reliability of Printed Circuit Board Assemblies

The effect of climatic conditions and ionic contamination on the reliability of printed circuit board assembly has been investigated in terms of leakage current (LC) and electrochemical migration susceptibility. The change in LC as a function of relative humidity (RH) and temperature was measured using single components (size 0805) and surface insulation resistance comb patterns precontaminated with sodium chloride at levels adjacent to levels used in the IPC J-STD-001 standard. The potential bias of 5-10 V was applied during experiments, and the climatic conditions were in the range 60%-98% RH and 15 °C-65 °C. The variation of RH at the surface of the test specimens was imposed by 1) increasing the RH of the surrounding air and 2) reducing the temperature of the printed circuit boards using a cooling stage, while maintaining a constant climatic condition in the chamber. A considerable increase in LC was observed at sodium chloride concentrations above 1.56 μg·cm-2, as the RH on the surface was close to the critical RH for sodium chloride. Prolonged exposure to conditions close to condensation resulted in the formation of tin whiskers and hillocks growing from the component electrodes due to corrosion of the electrodes freeing the whisker growth.

[1]  R. Ambat,et al.  Effect of solder flux residues on corrosion of electronics , 2009, 2009 Annual Reliability and Maintainability Symposium.

[2]  G. W. Warren,et al.  The role of electrochemical migration and moisture adsorption on the reliability of metallized ceramic substrates , 1989 .

[4]  Rajan Ambat,et al.  On the electrochemical migration mechanism of tin in electronics , 2011 .

[5]  M. Tencer,et al.  Humidity management of outdoor electronic equipment: methods, pitfalls, and recommendations , 2002 .

[6]  H. Cui.  Accelerated temperature cycle test and Coffin-Manson model for electronic packaging , 2005, Annual Reliability and Maintainability Symposium, 2005. Proceedings..

[7]  U. Pöschl,et al.  Mass-based hygroscopicity parameter interaction model and measurement of atmospheric aerosol water uptake , 2011 .

[8]  R. Ambat,et al.  Investigation of Electronic Corrosion Mechanisms , 2010 .

[9]  Rajan Ambat,et al.  Electrochemical migration of tin in electronics and microstructure of the dendrites , 2011 .

[10]  The role of water vapour in the corrosion of microelectronic circuits , 1977 .

[11]  M. J. Cushing,et al.  Comparison of electronics-reliability assessment approaches , 1993 .

[12]  S. J. Krumbein,et al.  Metallic electromigration phenomena , 1988 .

[13]  M.H. Azarian,et al.  Reliability of Printed Circuit Boards Processed Using No-Clean Flux Technology in Temperature–Humidity–Bias Conditions , 2008, IEEE Transactions on Device and Materials Reliability.

[14]  K. Tu.  Spontaneous Tin Whisker Growth: Mechanism and Prevention , 2007 .

[15]  P. Vianco,et al.  Quantitative analysis for hillocks grown from electroplated Sn film , 2010 .

[16]  M. Jellesen,et al.  Influence of sodium chloride and weak organic acids (flux residues) on electrochemical migration of tin on surface mount chip components , 2013 .

[17]  Microstructural rearrangement of sodium chloride condensation aerosol particles on interaction with water vapor , 2000 .

[18]  R. L. Shook,et al.  Sn whiskers: material, design, processing, and post-plate reflow effects and development of an overall phenomenological theory , 2005, IEEE Transactions on Electronics Packaging Manufacturing.

[19]  Roger Rörgren,et al.  Reliability of BGA Packages in an Automotive Environment , 1999 .

[20]  Douglas Pauls.  Residues in printed wiring boards and assemblies , 2001 .

[21]  Rajan Ambat,et al.  Corrosion failure due to flux residues in an electronic add-on device , 2010 .

[22]  B. Brox,et al.  Reliability of Electronics in Harsh Environments , 1995 .

[23]  Y. Chan,et al.  Effects of intermetallic compounds on properties of Sn-Cu lead-free soldered joints , 2005, Proceedings of 2005 International Conference on Asian Green Electronics, 2005. AGEC..

[24]  C. Hunt,et al.  The impact of temperature and humidity conditions on surface insulation resistance values for various fluxes , 1999 .

[25]  H. F. Hamann,et al.  Corrosion risk management in IT facilities , 2012, 13th InterSociety Conference on Thermal and Thermomechanical Phenomena in Electronic Systems.

[26]  P. Tegehall.  Impact of Humidity and Contamination on Surface Insulation Resistance and Electrochemical Migration , 2011 .

[27]  F. Cirolia,et al.  The effects of airborne contaminants on electronic power supplies , 2001, APEC 2001. Sixteenth Annual IEEE Applied Power Electronics Conference and Exposition (Cat. No.01CH37181).

[28]  C. Weschler,et al.  Deposition of Airborne Sulfate, Nitrate, and Chloride Salts as It Relates to Corrosion of Electronics , 1990 .

[29]  J. E. Sohn,et al.  Weak Organic Acids and Surface Insulation Resistance , 1995 .

[30]  M. Tencer.  Conductive aqueous layer formation at the gel-substrate interface in equilibrium with 100% RH environment , 2000 .

[31]  Peng Su,et al.  A Statistical Study of Sn Whisker Population and Growth During Elevated Temperature and Humidity Tests , 2006, IEEE Transactions on Electronics Packaging Manufacturing.

[32]  Sheng Zhan,et al.  Surface Insulation Resistance of Conformally Coated Printed Circuit Boards Processed With No-Clean Flux , 2006, IEEE Transactions on Electronics Packaging Manufacturing.

[33]  Y. Lai,et al.  Blocking hillock and whisker growth by intermetallic compound formation in Sn-0.7Cu flip chip solder joints under electromigration , 2010 .

[34]  S. Herminghaus,et al.  Wetting: Statics and dynamics , 1997 .

[35]  Reima Lahtinen,et al.  Corrosion and climatic effects in electronics , 2000 .

[36]  G. Harsányi,et al.  Effects of Flux Residues on Surface Insulation Resistance and Electrochemical Migration , 2006, 2006 29th International Spring Seminar on Electronics Technology.

[37]  Gery R. Stafford,et al.  Whisker and Hillock formation on Sn, Sn–Cu and Sn–Pb electrodeposits , 2005 .

[38]  J. P. Hartnett,et al.  Steam and air tables in SI units : including data for other substances with a separate Mollier chart for steam , 1976 .

[39]  Cedar Rapids,et al.  Process Qualification Using the IPC-B-52 Standard Test Assembly , 2006 .

[40]  Barbara Horváth,et al.  Effect of strongly oxidizing environment on whisker growth form tin coating , 2010 .

[41]  Sayoon Kang,et al.  Growth of tin whiskers for lead-free plated leadframe packages in high humid environments and during thermal cycling , 2007, Microelectron. Reliab..

[42]  A. Steinke,et al.  Failure of electronic devices due to condensation , 2008 .

[43]  R. Ambat,et al.  Electrochemical Migration on Electronic Chip Resistors in Chloride Environments , 2009, IEEE Transactions on Device and Materials Reliability.

[44]  R. Ambat,et al.  Effect of No-Clean Flux Residues on the Performance of Acrylic Conformal Coating in Aggressive Environments , 2012, IEEE Transactions on Components, Packaging and Manufacturing Technology.

[45]  C. E. Hoge.  Corrosion criteria for electronic packaging. III. Corrosion by package family , 1990 .