Threshold chloride level and characteristics of reinforcement corrosion initiation in simulated concrete pore solutions

Abstract Threshold chloride level (Cth) and corrosion behavior of reinforced steel bar (rebar) have been studied in three kinds of simulated concrete pore solutions (SPSs). The rebars with two different surface conditions were immersed in SPSs and open circuit potential (OCP) and linear polarization resistance (LPR) were monitored with stepwise chloride addition. Different electrochemical techniques for Cths and rebar corrosion initiation of all cases are discussed and compared with results from the literature. The results indicate that Cths acquired from both OCP and LPR techniques are relatively consistent. Cths, represented by the threshold expression [Cl−] or [Cl−]/[OH−], exhibit an increasing trend with increasing SPS pH. Corrosion resistance of both sandblasted and prerusted bars can be improved by raising the pH of the SPS solution; the extent of improvement is more pronounced for sandblasted bars. Once initiated, severe pit corrosion occurs on sandblasted bars with more abrupt OCP and corrosion current density variation exhibited.

[1]  A. Sagüés,et al.  Effect of Chloride Concentration on the Pitting and Repassivation Potentials of Reinforcing Steel in Alkaline Solutions , 1999 .

[2]  V. Gouda.  Corrosion and Corrosion Inhibition of Reinforcing Steel: I. Immersed in Alkaline Solutions , 1970 .

[3]  John R. Scully,et al.  Chloride Threshold Levels in Clad 316L and Solid 316LN Stainless Steel Rebar , 2002 .

[4]  David Trejo,et al.  Accelerated Chloride Threshold Testing: Part I-ASTM A 615 and A 706 Reinforcement , 2003 .

[5]  Odd E. Gjørv,et al.  Diffusion of chloride ions from seawater into concrete , 1979 .

[6]  T. Yonezawa,et al.  Pore Solution Composition and Chloride Effects on the Corrosion of Steel in Concrete , 1988 .

[7]  Luca Bertolini,et al.  Chloride threshold for rebar corrosion in concrete with addition of silica fume , 2008 .

[8]  Ki Yong Ann,et al.  Chloride threshold level for corrosion of steel in concrete , 2007 .

[9]  Tamon Ueda,et al.  Performance-based Standard Specifications for Maintenance and Repair of Concrete Structures in Japan , 2007 .

[10]  Duan Weng,et al.  A time-saving method to determine the chloride threshold level for depassivation of steel in concrete , 2010 .

[11]  C. Andrade,et al.  Chloride threshold values to depassivate reinforcing bars embedded in a standardized OPC mortar , 2000 .

[12]  Jinxia Xu,et al.  Influence of detection methods on chloride threshold value for the corrosion of steel reinforcement , 2009 .

[13]  A. Sagüés,et al.  Chloride Corrosion Threshold of Reinforcing Steel in Alkaline Solutions—Cyclic Polarization Behavior , 2002 .

[14]  H. Wheat,et al.  Effect of Chlorides on Reinforcing Steel Exposed to Simulated Concrete Solutions , 1997 .

[15]  G. Glass,et al.  The presentation of the chloride threshold level for corrosion of steel in concrete , 1997 .

[16]  W. Breit,et al.  Kritischer Chloridgehalt – Untersuchungen an Stahl in chloridhaltigen alkalischen Lösungen , 1998 .

[17]  Ueli Angst,et al.  Critical Chloride Content in Reinforced Concrete: A Review , 2009 .

[18]  D. Hausmann,et al.  STEEL CORROSION IN CONCRETE -- HOW DOES IT OCCUR? , 1967 .

[19]  Josef Tritthart,et al.  Chloride binding in cement II. The influence of the hydroxide concentration in the pore solution of hardened cement paste on chloride binding , 1989 .

[20]  Alberto A. Sagüés,et al.  Chloride Corrosion Threshold of Reinforcing Steel in Alkaline Solutions—Open-Circuit Immersion Tests , 2001 .

[21]  Brian B. Hope,et al.  The influence of surface finish of reinforcing steel and ph of the test solution on the chloride threshold concentration for corrosion initiation in synthetic pore solutions , 1996 .

[22]  C. Andrade,et al.  Synthetic concrete pore solution chemistry and rebar corrosion rate in the presence of chlorides , 1990 .

[23]  Effects Of Reinforcement And Coarse Aggregates On Chloride Ingress And Time-To-Corrosion: Part II - Spatial Distribution of Coarse Aggregates , 2007 .

[24]  Tarek Uddin Mohammed,et al.  Corrosion of Steel Bars in Concrete with Various Steel Surface Conditions , 2006 .

[25]  W. Hartt,et al.  Laboratory investigation of reinforcement corrosion initiation and chloride threshold content for self-compacting concrete , 2010 .

[26]  William H. Hartt,et al.  Effects of Reinforcement and Coarse Aggregates on Chloride Ingress into Concrete and Time-to-Corrosion: Part 1—Spatial Chloride Distribution and Implications , 2007 .