Effect of the dispersibility of nano-CuO catalyst on heat releasing of AP/HTPB propellant

Kneading time is adjusted to change the dispersibility of nano-CuO in AP/HTPB (Ammonia Perchlorate/Hydroxyl-Terminated Polybutadiene) composite propellants. Nano-CuO/AP is prepared to serve as the other dispersing method of nano-CuO, named predispersing procedure. Several kinds of heat releasing, thermal decomposition by DSC, combustion heat in oxygen environment, and explosion heat in nitrogen environment, are characterized to learn the effect of dispersibility of nano-CuO catalyst on heat releasing of propellants.With pre-dispersing procedures, thermal decomposition temperature of nano-CuO/AP and its propellant are about 25°C and 8.6°C lower than that of AP simple mixed with nano-CuO and its propellant, respectively. Comparing propellant with simple mixed nano-CuO kneading 3 hours, combustion heat and explosion heat of propellant with nano-CuO/AP increase about 1.4% and 1.7%, respectively.However, because of the breaking of nano-CuO/AP structure during kneading procedure, combustion heat and explosion heat of all the samples are decreased with the increase of kneading time after 3 hours.

Yi Yang | Ya-xiao Wang | Jun Wang | Xin Yu

[1] Xin Wang,et al. Preparation of NdCrO3 nanoparticles and their catalytic activity in the thermal decomposition of ammonium perchlorate by DSC/TG-MS , 2009 .

[2] Yue-hua Hu,et al. Dispersion mechanism of nano-magnetite coated with oleate in aqueous carrier , 2008 .

[3] L. P. Li,et al. Thermal decomposition of ammonium perchlorate activated via addition of NiO nanocrystals , 2008 .

[4] Xin Wang,et al. Preparation of novel structural nanosized Y2O3 powders and their catalytic activity on the decomposition of NH4ClO4 , 2007 .

[5] Carole Rossi,et al. Development of a nano-Al∕CuO based energetic material on silicon substrate , 2007 .

[6] Rongguo Wang,et al. Dispersibility and Degradation Properties Characterization of Nano Titanium Dioxide Photocatalysis Material , 2007 .

[7] Masahide Kawaraya. Dispersibility of Nano-TiO2 Paste with Fine Ceramic Beads and Morphology of the Mesoporous Film , 2007 .

[8] Qianwang Chen,et al. Ni hollow nanospheres: preparation and catalytic activity , 2006 .

[9] Feng-sheng Li,et al. Effects of Nanometer Ni, Cu, Al and NiCu Powders on the Thermal Decomposition of Ammonium Perchlorate , 2004 .

[10] V. F. Komarov. Catalysis and inhibition of the combustion of ammonium perchlorate based solid propellants , 1999 .

[11] A. Said,et al. The Role of Copper Cobaltite Spinel, CuxCo3‐xO4 During the Thermal Decomposition of Ammonium Perchlorate. , 1996 .