Adhesion properties of arc ion-plated TiN coatings with WC particle size, Co content and surface roughness

Abstract In this work, TiN coating layers were deposited on various kinds of WC–Co substrates by an arc ion plating (AIP) method. Effects of WC particle size, Co content, surface roughness on the adhesion strength and failure behavior of the AIP-TiN/substrate interface were studied using a conventional scratch test. It was found that Co had diffused out of the substrate toward the coating layer and formed a certain phase composed of Ti and Co. This phenomenon might induce strong bonding between the coating layer and the substrate. The highest critical load, approximately 110 N, was obtained at a WC particle size of 1 μm and Co content of 10 wt.%. As the WC particle size, Co content and surface roughness of the substrate increased, the critical load was reduced. Adhesion between the coating and substrate was considerably affected by both the surface morphology of the coating and the surface roughness of the substrate.

[1]  H. Ollendorf,et al.  A comparative study of adhesion test methods for hard coatings , 1999 .

[2]  T. Cselle,et al.  Today's applications and future developments of coatings for drills and rotating cutting tools , 1995 .

[3]  W. Ho,et al.  Effect of substrate surface roughness on the characteristics of CrN hard film , 1996 .

[4]  L. Karlsson,et al.  Microstructural investigation of droplets in arc-evaporated TiN films , 1994 .

[5]  Improvement of adhesion of TiN coatings on stainless steel substrates by high energy heavy ion irradiation , 1995 .

[6]  J. Vossen,et al.  Contemporary preparative techniques , 1989 .

[7]  T. Nsongo,et al.  Adhesion characterization of titanium and titanium nitride thin coatings on metals using the scratch test , 1995 .

[8]  I. Ansara,et al.  Thermodynamic modelling of the Co–Ti system , 2000 .

[9]  A. Perry,et al.  Low-temperature deposition of titanium nitride , 1995 .

[10]  Combination of scratch-test and acoustic microscopy imaging for the study of coating adhesion , 1997 .

[11]  D. S. Rickerby,et al.  The relationship between hardness and scratch adhession , 1987 .

[12]  F. Hauser,et al.  Deformation and Fracture Mechanics of Engineering Materials , 1976 .

[13]  Young-cheol Kim,et al.  The effect of NH3 plasma pre-treatment on the properties of TiN coatings produced by plasma-enhanced chemical vapor deposition (PECVD) , 1999 .

[14]  P. Steinmann,et al.  A review of the mechanical tests for assessment of thin‐film adhesion , 1989 .

[15]  F. Nabarro,et al.  Semi-empirical relationship between the hardness, grain size and mean free path of WC–Co , 2001 .

[16]  H. Uchida,et al.  A study on the surface structure of Ti cathode and the macroparticle of TiN films prepared by the arc ion plating process , 1996 .

[17]  R. Cremer,et al.  Composition, binding states, structure, and morphology of the corrosion layer of an oxidized Ti0.46Al0.54N film , 1998 .

[18]  M. T. Vieira,et al.  The influence of ductile interlayers on the mechanical performance of tungsten nitride coatings , 1999 .

[19]  Y. Pauleau,et al.  Adhesion and failure mechanisms of tungsten-carbon containing multilayered and graded coatings subjected to scratch tests , 1999 .

[20]  T. Sakakibara,et al.  Excitation, ionization, and reaction mechanism of a reactive cathodic arc deposition of TiN , 1994 .

[21]  J. Daalder Cathode spots and vacuum arcs , 1981 .

[22]  H. Ichimura,et al.  The correlation of scratch adhesion with composite hardness for TiN coatings , 2000 .

[23]  M. Ristova,et al.  XPS profile analysis on CdS thin film modified with Ag by an ion exchange , 2001 .

[24]  N. Axén,et al.  A model for the hardness of cemented carbides , 2002 .

[25]  J. Gurland,et al.  Relation of Strength, Composition, and Grain Size of Sintered WC-Co Alloys , 1955 .

[26]  Yue Zhang,et al.  Study on the relation between structural parameters and fracture strength of WC-Co cemented carbides , 2000 .