Microstructure control of thermally stable TiO2 obtained by hydrothermal process for gas sensors

Abstract Nanocrystalline titanium dioxide with enhanced thermal stability was prepared by subjecting the alkoxide-derived TiO 2 gel to a hydrothermal treatment at 150 °C for 3 h in dilute HNO 3 solution (pH 3 or 2). Structural modifications of TiO 2 were analyzed by XRD and the morphology of the powders observed by FE-SEM. The hydrothermal treatment stabilized TiO 2 in two ways, i.e., suppressing thermal growth of TiO 2 crystallites and shifting up the temperature of anatase-to-rutile phase transformation, although the degree of stabilization differed considerably depending on the pH of the HNO 3 solution used. The TiO 2 hydrothermally treated at pH 3 consisted of small anatase nanospheres of 13 and 34 nm in average diameter after calcination at 600 and 800 °C, respectively, whereas the untreated TiO 2 was predominated by rutile phase at 700 °C. Suppression of crystallite growth was even more conspicuous with the treatment at pH 2; the average crystallite size of anatase was 11 and 26 nm after calcined at 600 and 800 °C, respectively. In this case, however, the transformation was less hindered, with rutile phase occupying 9, 22 and 67% of TiO 2 after calcinations at 600, 700 and 800 °C, respectively. This indicates that the phase transformation is not always related uniquely with crystallite size of anatase phase. The thick films fabricated with these TiO 2 powders did not show much differences in sensor response (ratio of resistance in air to that in gas) to dilute CO in air at 400–550 °C, though the powder hydrothermally treated at pH 3 tended to give the highest response. However, the hydrothermal treatment was found to improve much the sensor response transients, suggesting that it was effective in developing mesopores inside the films.

[1]  Jordi Arbiol,et al.  Study of the influence of Nb content and sintering temperature on TiO2 sensing films , 2003 .

[2]  N. Yamazoe,et al.  Hydrothermal treatment of tin oxide sol solution for preparation of thin-film sensor with enhanced thermal stability and gas sensitivity , 2000 .

[3]  Wolfgang Göpel,et al.  Chemical sensing, molecular electronics and nanotechnology: Interface technologies down to the molecular scale , 1991 .

[4]  Yaoqiang Chen,et al.  An investigation of the preparation of TiO2-based catalysts using methods of thermal analysis , 1994 .

[5]  Sheikh A. Akbar,et al.  Sensing Mechanism of a Carbon Monoxide Sensor Based on Anatase Titania , 1997 .

[6]  Norio Miura,et al.  Gas sensing properties of tin oxide thin films fabricated from hydrothermally treated nanoparticles: Dependence of CO and H2 response on film thickness , 2001 .

[7]  L. Bergström,et al.  The effect of acids and bases on the dispersion and stabilization of ceramic particles in ethanol , 2000 .

[8]  David E. Williams Semiconducting oxides as gas-sensitive resistors , 1999 .

[9]  Joan Ramon Morante,et al.  Study of La and Cu influence on the growth inhibition and phase transformation of nano-TiO2 used for gas sensors , 2004 .

[10]  Kengo Shimanoe,et al.  Cr-doped TiO2 gas sensor for exhaust NO2 monitoring , 2003 .

[11]  A. Nakano,et al.  Role of atomic charge transfer on sintering of TiO2 nanoparticles: Variable-charge molecular dynamics , 2000 .

[12]  N. Bârsan,et al.  Micromachined metal oxide gas sensors: opportunities to improve sensor performance , 2001 .

[13]  Norio Miura,et al.  Hydrothermally treated sol solution of tin oxide for thin-film gas sensor , 2000 .