Violet-blue LEDs based on p-GaN/n-ZnO nanorods and their stability

In this paper, we report a fabrication, characterization and stability study of p-GaN/n-ZnO nanorod heterojunction light-emitting devices (LEDs). The LEDs were assembled from arrays of n-ZnO vertical nanorods epitaxially grown on p-GaN. LEDs showed bright electroluminescence in blue (440 nm), although weaker violet (372 nm) and green-yellow (550 nm) spectral components were also observed. The device characteristics are generally stable and reproducible. The LEDs have a low turn-on voltage (∼5 V). The electroluminescence (EL) is intense enough to be noticed by the naked eye, at an injection current as low as ∼ 40 µA (2.1 × 10(-2) A cm(-2) at 7 V bias). Analysis of the materials, electrical and EL investigations point to the role of a high quality of p-n nano-heterojunction which facilitates a large rectification ratio (320) and a stable reverse current of 2.8 µA (1.4 × 10(-3) A cm(-2) at 5 V). Stability of EL characteristics was investigated in detail. EL intensity showed systematic degradation over a short duration when the LED was bias-stressed at 30 V. At smaller bias (<20 V) LEDs tend to show a stable and repeatable EL characteristic. Thus a simple low temperature solution growth method was successfully exploited to realize nanorod/film heterojunction LED devices with predictable characteristics.

[1]  T. M. Klapwijk,et al.  Scaling of nano-Schottky-diodes , 2002 .

[2]  Young Joon Hong,et al.  GaN/In1-xGaxN/GaN/ZnO nanoarchitecture light emitting diode microarrays , 2009 .

[3]  H. L. Tam,et al.  GaN/ZnO nanorod light emitting diodes with different emission spectra , 2009, Nanotechnology.

[4]  S. Studenikin,et al.  Time-resolved luminescence and photoconductivity of polycrystalline ZnO films , 2002 .

[5]  Peidong Yang,et al.  Vertical nanowire array-based light emitting diodes , 2008 .

[6]  O. Nur,et al.  The effect of the post-growth annealing on the electroluminescence properties of n-ZnO nanorods/p-GaN light emitting diodes , 2010 .

[7]  Takafumi Yao,et al.  Band alignment at a ZnO/GaN (0001) heterointerface , 2001 .

[8]  Jae-Young Choi,et al.  Morphology Control and Electroluminescence of ZnO Nanorod/GaN Heterojunctions Prepared Using Aqueous Solution , 2009 .

[9]  Moon-Ho Ham,et al.  ZnO-nanowire-inserted GaN/ZnO heterojunction light-emitting diodes. , 2007, Small.

[10]  Chang-Hee Hong,et al.  Magnesium acceptor levels in GaN studied by photoluminescence , 1998 .

[11]  Peidong Yang,et al.  Nanowire dye-sensitized solar cells , 2005, Nature materials.

[12]  Zhong Lin Wang,et al.  Large-Scale Hexagonal-Patterned Growth of Aligned ZnO Nanorods for Nano-optoelectronics and Nanosensor Arrays. , 2004, Nano letters.

[13]  Yu Huang,et al.  Indium phosphide nanowires as building blocks for nanoscale electronic and optoelectronic devices , 2001, Nature.

[14]  Peidong Yang,et al.  Optical Cavity Effects in ZnO Nanowire Lasers and Waveguides , 2003 .

[15]  W. Park,et al.  Electroluminescence in n‐ZnO Nanorod Arrays Vertically Grown on p‐GaN , 2004 .

[16]  Integrated Nanorods and Heterostructure Field Effect Transistors for Gas Sensing , 2010 .

[17]  Yiying Wu,et al.  Room-Temperature Ultraviolet Nanowire Nanolasers , 2001, Science.

[18]  S. An,et al.  Near ultraviolet light emitting diode composed of n-GaN∕ZnO coaxial nanorod heterostructures on a p-GaN layer , 2007 .

[19]  J.A. del Alamo,et al.  A Simple Current Collapse Measurement Technique for GaN High-Electron Mobility Transistors , 2008, IEEE Electron Device Letters.

[20]  Xiao-mei Zhang,et al.  Fabrication of a High‐Brightness Blue‐Light‐Emitting Diode Using a ZnO‐Nanowire Array Grown on p‐GaN Thin Film , 2009 .

[21]  Wi Hyoung Lee,et al.  High-mobility low-temperature ZnO transistors with low-voltage operation , 2010 .

[22]  H. Morkoç,et al.  A COMPREHENSIVE REVIEW OF ZNO MATERIALS AND DEVICES , 2005 .