Experimental evidence for voltage driven breakdown models in ultrathin gate oxides

We have performed an experiment proving that the widely accepted E-field TDDB model is a physically incorrect description of breakdown in ultrathin gate oxides. Although interface traps are the dominant SILC mechanism below 5 V stress, breakdown remains limited by bulk trap generation and is voltage-driven. It has been recently proposed that the anode hole injection model is still operative at low voltages. Although we will show that holes do generate bulk traps and cause breakdown in ultrathin oxides, hole injection does not completely account for all of the trap generation mechanisms observed during direct tunneling stress.

[1]  Douglas A. Buchanan,et al.  Hot-electron-induced hydrogen redistribution and defect generation in metal-oxide-semiconductor capacitors , 1994 .

[2]  R. Degraeve,et al.  Photo-carrier generation as the origin of Fowler-Nordheim-induced substrate hole current in thin oxides , 1999, International Electron Devices Meeting 1999. Technical Digest (Cat. No.99CH36318).

[3]  E. S. Anolick,et al.  Low-Field Time-Dependent Dielectric Integrity , 1979, IEEE Transactions on Reliability.

[4]  Prasad Chaparala,et al.  Field and temperature acceleration of time-dependent dielectric breakdown in intrinsic thin SiO/sub 2/ , 1994, Proceedings of 1994 IEEE International Reliability Physics Symposium.

[5]  Robert M. Wallace,et al.  Low voltage stress-induced-leakage-current in ultrathin gate oxides , 1999, 1999 IEEE International Reliability Physics Symposium Proceedings. 37th Annual (Cat. No.99CH36296).

[6]  Thomas H. DiStefano,et al.  Impact ionization model for dielectric instability and breakdown , 1974 .

[7]  D. Dimaria,et al.  Explanation for the polarity dependence of breakdown in ultrathin silicon dioxide films , 1996 .

[8]  Ernest Y. Wu,et al.  Challenges for accurate reliability projections in the ultra-thin oxide regime , 1999, 1999 IEEE International Reliability Physics Symposium Proceedings. 37th Annual (Cat. No.99CH36296).

[9]  Masakazu Shimaya,et al.  Neutral electron trap generation in SiO2 by hot holes , 1990 .

[10]  C. Hu,et al.  Stress-induced current in thin silicon dioxide films , 1992, 1992 International Technical Digest on Electron Devices Meeting.

[11]  Dwight L. Crook,et al.  Method of Determining Reliability Screens for Time Dependent Dielectric Breakdown , 1979, 17th International Reliability Physics Symposium.

[12]  P.J. Silverman,et al.  Explanation of stress-induced damage in thin oxides , 1998, International Electron Devices Meeting 1998. Technical Digest (Cat. No.98CH36217).

[13]  D. Wristers,et al.  Polarity dependence of dielectric breakdown in scaled SiO/sub 2/ , 1994, Proceedings of 1994 IEEE International Electron Devices Meeting.

[14]  J. Stathis,et al.  Reliability projection for ultra-thin oxides at low voltage , 1998, International Electron Devices Meeting 1998. Technical Digest (Cat. No.98CH36217).

[15]  A. Toriumi,et al.  Experimental evidence of inelastic tunneling and new I-V model for stress-induced leakage current , 1996, International Electron Devices Meeting. Technical Digest.

[16]  T. Nigam,et al.  Temperature acceleration of oxide breakdown and its impact on ultra-thin gate oxide reliability , 1999, 1999 Symposium on VLSI Technology. Digest of Technical Papers (IEEE Cat. No.99CH36325).

[17]  G. Klimeck,et al.  Physical oxide thickness extraction and verification using quantum mechanical simulation , 1997, International Electron Devices Meeting. IEDM Technical Digest.

[18]  James Stasiak,et al.  Trap creation in silicon dioxide produced by hot electrons , 1989 .

[19]  S. Lai,et al.  Interface trap generation in silicon dioxide when electrons are captured by trapped holes , 1983 .

[20]  C. Hu,et al.  Hole injection SiO/sub 2/ breakdown model for very low voltage lifetime extrapolation , 1994 .

[21]  E. Cartier,et al.  MECHANISM FOR STRESS-INDUCED LEAKAGE CURRENTS IN THIN SILICON DIOXIDE FILMS , 1995 .

[22]  C. Hu,et al.  A unified gate oxide reliability model , 1999, 1999 IEEE International Reliability Physics Symposium Proceedings. 37th Annual (Cat. No.99CH36296).

[23]  S. Holland,et al.  A quantitative physical model for time-dependent breakdown in SiO2 , 1985, 23rd International Reliability Physics Symposium.

[24]  Elyse Rosenbaum,et al.  Mechanism of stress-induced leakage current in MOS capacitors , 1997 .

[25]  Eduard A. Cartier,et al.  Anode hole injection and trapping in silicon dioxide , 1996 .

[26]  Chenming Hu,et al.  Temperature acceleration of time-dependent dielectric breakdown , 1989 .

[27]  F. J. Feigl,et al.  Positive charge generation in metal‐oxide‐semiconductor capacitors , 1991 .