Effect of moisture content on concrete resistivity measurement

Abstract The resistivity of concrete was investigated in this study by employing the Wenner technique. Cylindrical specimens with various water/cement ratios (w/c=0.45, 0.55, and 0.65) were cast and tested. In order to study the effect of moisture content on concrete resistivity, the resistivity and weight were measured for air‐dried specimens and oven‐dried specimens. Test results show that the resistivity decreases with an increase in w/c ratio, but for the saturated concrete specimens with high w/c ratios (w/c>0.55) the resistivity difference is small. For specimens after 8‐hours of air drying, the water loss ratio was about 0.7% and the normalized resistivity increased from 5% to 10% in comparison with the saturated concrete specimens. When the water loss ratio was higher than 3%, the concrete resistivity abruptly increased for all mixes. Therefore, the effect of moisture content on concrete resistivity measurement should be considered in durability evaluation.

[1]  James J. Beaudoin,et al.  Pore structure of hardened portland cement pastes and its influence on properties , 1994 .

[2]  A. M. Brandt.  Cement-based Composites: Materials, Mechanical Properties and Performance , 1995 .

[3]  R. D. Browner.  Design prediction of the life for reinforced concrete in marine and other chloride environments , 1982 .

[4]  Pierre-Claude Aitcin,et al.  Concrete structure, properties and materials , 1986 .

[5]  F. Hunkeler.  THE RESISTIVITY OF PORE WATER SOLUTION - A DECISIVE PARAMETER OF REBAR CORROSION AND REPAIR METHODS , 1996 .

[6]  Steve Millard,et al.  Measurement of concrete resistivity for assessment of corrosion severity of steel using wenner technique , 1999 .

[7]  Alberto A. Sagüés,et al.  Practical evaluation of resistivity of concrete in test cylinders using a Wenner array probe , 1996 .

[8]  D. Chung,et al.  Sensitivity of the bond strength to the structure of the interface between reinforcement and cement, and the variability of this structure , 1998 .

[9]  W. López,et al.  Effects of Moisture Availability on Corrosion Kinetics of Steel Embedded in Concrete , 1993 .

[10]  D. Hannant.  4.11 – Cement-based Composites , 2000 .

[11]  Kenneth C. Hover,et al.  Influence of microcracking on the mass transport properties of concrete , 1992 .

[12]  H. W. Whittington,et al.  The conduction of electricity through concrete , 1981 .

[13]  Pa Wedding,et al.  The Electrical Resistivity of Concrete with Emphasis on the Use of Electrical Resistance for Measuring Moisture Content , 1979 .