Optical Absorption Enhancement in Freestanding GaAs Thin Film Nanopyramid Arrays

Although III–V compound semiconductor multi‐junction cells show the highest efficiency among all types of solar cells, their cost is quite high due to expensive substrates, long epitaxial growth and complex balance of system components. To reduce the cost, ultra‐thin films with advanced light management are desired. Here effective light trapping in freestanding thin film nanopyramid arrays is demonstrated and multiple‐times light path enhancement is realized, where only 160 nm thick GaAs with nanopyramid structures is equivalent to a 1 μm thick planar film. The GaAs nanopyramids are fabricated using a combination of nanosphere lithography, nanopyramid metal organic chemical vapor deposition (MOCVD) growth, and gas‐phase substrate removal processes. Excellent optical absorption is demonstrated over a broad range of wavelengths, at various incident angles and at large‐curvature bending. Compared to an equally thick planar control film, the overall number of photons absorbed is increased by about 100% at various incident angles due to significant antireflection and light trapping effects. By implementing these nanopyramid structures, III–V material usage and deposition time can be significantly reduced to produce high‐efficiency, low‐cost thin film III–V solar cells.

[1]  Shanhui Fan,et al.  S4 : A free electromagnetic solver for layered periodic structures , 2012, Comput. Phys. Commun..

[2]  Guiling Li,et al.  Preparation and In Vitro Evaluation of Tacrolimus-Loaded Ethosomes , 2012, TheScientificWorldJournal.

[3]  Martin A. Green,et al.  Solar cell efficiency tables (Version 38) , 2011 .

[4]  Giacomo Mariani,et al.  Patterned radial GaAs nanopillar solar cells. , 2011, Nano letters.

[5]  Nathan S. Lewis,et al.  Si microwire-array solar cells , 2010 .

[6]  J. Lefebvre,et al.  Selective epitaxy of semiconductor nanopyramids for nanophotonics , 2010, Nanotechnology.

[7]  Markus Aspelmeyer,et al.  Free-standing AlxGa1−xAs heterostructures by gas-phase etching of germanium , 2010 .

[8]  Zongfu Yu,et al.  Nanodome solar cells with efficient light management and self-cleaning. , 2010, Nano letters.

[9]  J. Rogers,et al.  GaAs photovoltaics and optoelectronics using releasable multilayer epitaxial assemblies , 2010, Nature.

[10]  Peidong Yang,et al.  Light trapping in silicon nanowire solar cells. , 2010, Nano letters.

[11]  Zhiyong Fan,et al.  Three-dimensional nanopillar-array photovoltaics on low-cost and flexible substrates. , 2009, Nature materials.

[12]  Bozhi Tian,et al.  Coaxial Group Iii#nitride Nanowire Photovoltaics , 2009 .

[13]  D. Thompson,et al.  GaAs core--shell nanowires for photovoltaic applications. , 2009, Nano letters.

[14]  Zongfu Yu,et al.  Optical absorption enhancement in amorphous silicon nanowire and nanocone arrays. , 2009, Nano letters.

[15]  James S. Harris,et al.  Low surface roughness and threading dislocation density Ge growth on Si (0 0 1) , 2008 .

[16]  Martin A. Green,et al.  Solar Energy Conversion Toward 1 Terawatt , 2008 .

[17]  S. Chang,et al.  Cu2O/n-ZnO nanowire solar cells on ZnO:Ga/glass templates , 2007 .

[18]  J. van Deelen,et al.  Photon confinement in high-efficiency, thin-film III–V solar cells obtained by epitaxial lift-off , 2006 .

[19]  Nathan S. Lewis,et al.  Comparison of the device physics principles of planar and radial p-n junction nanorod solar cells , 2005 .

[20]  T. Ishihara,et al.  Quasiguided modes and optical properties of photonic crystal slabs , 2002 .

[21]  E. Palik.  Handbook of Optical Constants of Solids , 1997 .

[22]  Lifeng Li,et al.  New formulation of the Fourier modal method for crossed surface-relief gratings , 1997 .

[23]  O. Heavens.  Handbook of Optical Constants of Solids II , 1992 .

[24]  E. Yablonovitch,et al.  Extreme selectivity in the lift‐off of epitaxial GaAs films , 1987 .

[25]  K. Fujikawa,et al.  MOCVD GaAs growth on Ge (100) and Si (100) substrates , 1986 .

[26]  H. C. Casey,et al.  Concentration dependence of the absorption coefficient for n− and p−type GaAs between 1.3 and 1.6 eV , 1975 .