Nanoscale mapping of contact stiffness and damping by contact resonance atomic force microscopy

In this work, a new procedure is demonstrated to retrieve the conservative and dissipative contributions to contact resonance atomic force microscopy (CR-AFM) measurements from the contact resonance frequency and resonance amplitude. By simultaneously tracking the CR-AFM frequency and amplitude during contact AFM scanning, the contact stiffness and damping were mapped with nanoscale resolution on copper (Cu) interconnects and low-k dielectric materials. A detailed surface mechanical characterization of the two materials and their interfaces was performed in terms of elastic moduli and contact damping coefficients by considering the system dynamics and included contact mechanics. Using Cu as a reference material, the CR-AFM measurements on the patterned structures showed a significant increase in the elastic modulus of the low-k dielectric material compared with that of a blanket pristine film. Such an increase in the elastic modulus suggests an enhancement in the densification of low-k dielectric films during patterning. In addition, the subsurface response of the materials was investigated in load-dependent CR-AFM point measurements and in this way a depth dimension was added to the common CR-AFM surface characterization. With the new proposed measurement procedure and analysis, the present investigation provides new insights into characterization of surface and subsurface mechanical responses of nanoscale structures and the integrity of their interfaces.

[1]  Harald Fuchs,et al.  Conservative and dissipative tip-sample interaction forces probed with dynamic AFM , 1999 .

[2]  R. Proksch,et al.  Mapping nanoscale elasticity and dissipation using dual frequency contact resonance AFM , 2011, Nanotechnology.

[3]  R. Cook,et al.  Diameter-Dependent Radial and Tangential Elastic Moduli of ZnO Nanowires , 2007 .

[4]  V. Dravid,et al.  Ultrasound holography for noninvasive imaging of buried defects and interfaces for advanced interconnect architectures , 2009 .

[5]  Karen Willcox,et al.  Kinetics and kinematics for translational motions in microgravity during parabolic flight. , 2009, Aviation, space, and environmental medicine.

[6]  W. Arnold,et al.  Observation of local internal friction and plasticity onset in nanocrystalline nickel by atomic force acoustic microscopy , 2009 .

[7]  Habib Mohamadian,et al.  Various shape memory effects of stimuli-responsive shape memory polymers , 2013 .

[8]  Sergei V. Kalinin,et al.  Double-layer mediated electromechanical response of amyloid fibrils in liquid environment. , 2010, ACS nano.

[9]  B. Gotsmann,et al.  Dynamic force spectroscopy using the frequency modulation technique with constant excitation , 2003 .

[10]  Anthony B. Kos,et al.  Nanoscale elastic-property measurements and mapping using atomic force acoustic microscopy methods , 2005 .

[11]  J. Turner,et al.  Relationship between Q-factor and sample damping for contact resonance atomic force microscope measurement of viscoelastic properties , 2011 .

[12]  Daniele Passeri,et al.  Local indentation modulus characterization of diamondlike carbon films by atomic force acoustic microscopy two contact resonance frequencies imaging technique , 2006 .

[13]  Kei Kobayashi,et al.  Resonance tracking ultrasonic atomic force microscopy , 2002 .

[14]  J. Turner,et al.  Contact-resonance atomic force microscopy for viscoelasticity , 2008 .

[15]  R. Cook,et al.  Elastic moduli of faceted aluminum nitride nanotubes measured by contact resonance atomic force microscopy , 2009, Nanotechnology.

[16]  R. Cook,et al.  Compressive stress effect on the radial elastic modulus of oxidized Si nanowires. , 2010, Nano letters.

[17]  R. Cook,et al.  Mapping the elastic properties of granular Au films by contact resonance atomic force microscopy , 2008, Nanotechnology.

[18]  Oliver B. Wright,et al.  Vibrational dynamics of force microscopy: Effect of tip dimensions , 1997 .

[19]  P. Couturier Japan , 1988, The Lancet.

[20]  Ute Rabe,et al.  Vibrations of free and surface‐coupled atomic force microscope cantilevers: Theory and experiment , 1996 .

[21]  Ricardo Garcia,et al.  Measuring phase shifts and energy dissipation with amplitude modulation atomic force microscopy , 2006, Nanotechnology.

[22]  B. Gotsmann,et al.  Measurement of conservative and dissipative tip-sample interaction forces with a dynamic force microscope using the frequency modulation technique , 2001 .

[23]  K. Johnson Contact Mechanics: Frontmatter , 1985 .

[24]  Process Control and Physical Failure Analysis for Sub-100NM CU/Low-K Structures , 2008, 2008 International Interconnect Technology Conference.

[25]  Robert E. Geer,et al.  Nanomechanical defect imaging in premetal dielectrics for integrated circuits , 2004 .

[26]  Santiago D. Solares,et al.  Mapping of conservative and dissipative interactions in bimodal atomic force microscopy using open-loop and phase-locked-loop control of the higher eigenmode , 2011 .

[27]  Kazushi Yamanaka,et al.  Ultrasonic Atomic Force Microscope with Overtone Excitation of Cantilever , 1996 .

[28]  Anthony B. Kos,et al.  Mapping substrate/film adhesion with contact-resonance-frequency atomic force microscopy , 2006 .

[29]  Stephen Jesse,et al.  The band excitation method in scanning probe microscopy for rapid mapping of energy dissipation on the nanoscale , 2007, 0708.4248.

[30]  Olav Solgaard,et al.  An atomic force microscope tip designed to measure time-varying nanomechanical forces , 2007, Nature Nanotechnology.

[31]  Siqun Wang,et al.  Nanoscale characterization of natural fibers and their composites using contact-resonance force microscopy , 2010 .

[32]  Keiichi Nakamoto,et al.  Resonance frequency and Q factor mapping by ultrasonic atomic force microscopy , 2001 .

[33]  Anish Kumar,et al.  Elasticity mapping of precipitates in polycrystalline materials using atomic force acoustic microscopy , 2008 .

[34]  E. Zschech,et al.  Quantitative mapping of elastic properties of plasma-treated silica-based low-k films , 2006 .

[35]  M. Bohr,et al.  90 nm generation, 300 mm wafer low k ILD/Cu interconnect technology , 2003, Proceedings of the IEEE 2003 International Interconnect Technology Conference (Cat. No.03TH8695).

[36]  Fen Chen,et al.  Addressing Cu/Low-$k$ Dielectric TDDB-Reliability Challenges for Advanced CMOS Technologies , 2009, IEEE Transactions on Electron Devices.

[37]  W. Arnold,et al.  High-frequency response of atomic-force microscope cantilevers , 1997 .

[38]  Joost J. Vlassak,et al.  Indentation modulus of elastically anisotropic half spaces , 1993 .