Electrochemical activation of carbon cloth in aqueous inorganic salt solution for superior capacitive performance.

Carbon cloth (CC) is an inexpensive and highly conductive textile with excellent mechanical flexibility and strength; it holds great promise as an electrode material for flexible supercapacitors. However, pristine CC has such a low surface area and poor electrochemical activity that the energy storage capability is usually very poor. Herein, we report a green method, two-step electrochemical activation in an aqueous solution of inorganic salts, to significantly enhance the capacitance of CC for supercapacitor application. Micro-cracks, exfoliated carbon fiber shells, and oxygen-containing functional groups (OFGs) were introduced onto the surface of the carbon filament. This resulted in an enhancement of over two orders of magnitude in capacitance compared to that of the bare CC electrode, reaching up to a maximum areal capacitance of 505.5 mF cm(-2) at the current density of 6 mA cm(-2) in aqueous H2SO4 electrolyte. Electrochemical reduction of CC electrodes led to the removal of most electrochemically unstable surface OFGs, resulting in superior charging/discharging rate capability and excellent cycling stability. Although the activated CC electrode contained a high-level of surface oxygen functional groups (∼15 at%), it still exhibited a remarkable charging-discharging rate capability, retaining ∼88% of the capacitance when the charging rate increased from 6 to 48 mA cm(-2). Moreover, the activated CC electrode exhibited excellent cycling stability with ∼97% capacitance remaining after 10 000 cycles at a current density of 24 mA cm(-2). A symmetrical supercapacitor based on the activated CC exhibited an ideal capacitive behavior and fast charge-discharge properties. Such a simple, environment-friendly, and cost-effective strategy to activate CC shows great potential in the fabrication of high-performance flexible supercapacitors.

[1]  Dingshan Yu,et al.  Transforming Pristine Carbon Fiber Tows into High Performance Solid‐State Fiber Supercapacitors , 2015, Advanced materials.

[2]  Minghao Yu,et al.  A Novel Exfoliation Strategy to Significantly Boost the Energy Storage Capability of Commercial Carbon Cloth , 2015, Advanced materials.

[3]  Lifeng Yan,et al.  Reduced graphene oxide hydrogel film with a continuous ion transport network for supercapacitors. , 2015, Nanoscale.

[4]  Jie Liu,et al.  Making a commercial carbon fiber cloth having comparable capacitances to carbon nanotubes and graphene in supercapacitors through a "top-down" approach. , 2015, Nanoscale.

[5]  G. Han,et al.  Facile preparation of polypyrrole/graphene oxide nanocomposites with large areal capacitance using electrochemical codeposition for supercapacitors , 2014 .

[6]  Wei Huang,et al.  Heteroatom-doped graphene materials: syntheses, properties and applications. , 2014, Chemical Society reviews.

[7]  Tianyu Liu,et al.  Electrodeposition of vanadium oxide–polyaniline composite nanowire electrodes for high energy density supercapacitors , 2014 .

[8]  H. Fan,et al.  Hollow nickel nanocorn arrays as three-dimensional and conductive support for metal oxides to boost supercapacitive performance. , 2014, Nanoscale.

[9]  Dingshan Yu,et al.  Scalable synthesis of hierarchically structured carbon nanotube–graphene fibres for capacitive energy storage , 2014, Nature Nanotechnology.

[10]  Teng Zhai,et al.  Solid‐State Supercapacitor Based on Activated Carbon Cloths Exhibits Excellent Rate Capability , 2014, Advanced materials.

[11]  K. Müllen,et al.  Exfoliation of graphite into graphene in aqueous solutions of inorganic salts. , 2014, Journal of the American Chemical Society.

[12]  V. Presser,et al.  Carbons and Electrolytes for Advanced Supercapacitors , 2014, Advanced materials.

[13]  Yue Wu,et al.  Patterned graphene functionalization via mask-free scanning of micro-plasma jet under ambient condition , 2014 .

[14]  Jing Zhang,et al.  Paper-based solid-state supercapacitors with pencil-drawing graphite/polyaniline networks hybrid electrodes , 2013 .

[15]  M. H. Chakrabarti,et al.  Electrochemical approaches to the production of graphene flakes and their potential applications , 2013 .

[16]  Andreas Winter,et al.  Three‐Dimensional Nitrogen and Boron Co‐doped Graphene for High‐Performance All‐Solid‐State Supercapacitors , 2012, Advanced materials.

[17]  P. Taberna,et al.  On the molecular origin of supercapacitance in nanoporous carbon electrodes. , 2012, Nature materials.

[18]  Xinzhuang Fan,et al.  Reversible redox reaction on the oxygen-containing functional groups of an electrochemically modified graphite electrode for the pseudo-capacitance , 2011 .

[19]  Norio Shinya,et al.  Polyaniline-Coated Electro-Etched Carbon Fiber Cloth Electrodes for Supercapacitors , 2011 .

[20]  Hyun Joon Shin,et al.  Nitrogen-doped graphene for high-performance ultracapacitors and the importance of nitrogen-doped sites at basal planes. , 2011, Nano letters.

[21]  C. Su,et al.  High-quality thin graphene films from fast electrochemical exfoliation. , 2011, ACS nano.

[22]  Peihua Huang,et al.  Ultrahigh-power micrometre-sized supercapacitors based on onion-like carbon. , 2010, Nature nanotechnology.

[23]  Liangbing Hu,et al.  Carbon nanotube thin films: fabrication, properties, and applications. , 2010, Chemical reviews.

[24]  Yuyan Shao,et al.  Facile and controllable electrochemical reduction of graphene oxide and its applications , 2010 .

[25]  Lili Zhang,et al.  Carbon-based materials as supercapacitor electrodes. , 2009, Chemical Society reviews.

[26]  X. Xia,et al.  A green approach to the synthesis of graphene nanosheets. , 2009, ACS nano.

[27]  Ming Zhou,et al.  Controlled synthesis of large-area and patterned electrochemically reduced graphene oxide films. , 2009, Chemistry.

[28]  H. Dai,et al.  N-Doping of Graphene Through Electrothermal Reactions with Ammonia , 2009, Science.

[29]  Mykola Seredych,et al.  Combined Effect of Nitrogen‐ and Oxygen‐Containing Functional Groups of Microporous Activated Carbon on its Electrochemical Performance in Supercapacitors , 2009 .

[30]  R. Ruoff,et al.  Graphene-based ultracapacitors. , 2008, Nano letters.

[31]  Mykola Seredych,et al.  Surface functional groups of carbons and the effects of their chemical character, density and accessibility to ions on electrochemical performance , 2008 .

[32]  John R. Miller,et al.  Electrochemical Capacitors for Energy Management , 2008, Science.

[33]  Stephen A. Morin,et al.  Structure, composition, and chemical reactivity of carbon nanotubes by selective nitrogen doping , 2006 .

[34]  F. Béguin,et al.  Carbon materials for the electrochemical storage of energy in capacitors , 2001 .

[35]  B. Conway.  Electrochemical Supercapacitors: Scientific Fundamentals and Technological Applications , 1999 .

[36]  Hang Shi,et al.  Studies of activated carbons used in double-layer capacitors , 1998 .

[37]  Bruce Dunn,et al.  Deposition of Ruthenium Nanoparticles on Carbon Aerogels for High Energy Density Supercapacitor Electrodes , 1997 .

[38]  N. Kotov,et al.  Ultrathin graphite oxide–polyelectrolyte composites prepared by self‐assembly: Transition between conductive and non‐conductive states , 1996 .

[39]  W. Marsden.  I and J , 2012 .

[40]  C. Pittman,et al.  Surface characterization of electrochemically oxidized carbon fibers , 1999 .

[41]  J. D. Lopez-Gonzalez,et al.  Study of oxygen-containing groups in a series of graphite oxides: Physical and chemical characterization , 1995 .