Selection of a carbon-14 fixation form

This report summarizes work on the selection of a disposal form for carbon-14 produced during the production of nuclear power. Carbon compounds were screened on the basis of solubility, thermal stability, resistance to oxidation, cost and availability, compatibility with the selected disposal matrix, leach resistance when incorporated in concrete, and compatibility with capture technologies. Carbonates are the products of the various technologies presently considered for carbon-14 capture. The alkaline earth carbonates exhibit the greatest thermal stabilities, lowest solubilities, lowest raw material cost, and greatest raw material availabilities. When reactions with cement and its impurities are considered, calcium and strontium carbonates are the only alkaline earth carbonates resistant to hydrolysis and reaction with sulfate. Leaching tests of barium, calcium, lead, potassium, and strontium carbonates in concrete showed calcium carbonate concrete to be slightly superior to the other alkaline earth carbonates, and greatly superior to a soluble carbonate, potassium carbonate, and lead carbonate. None of the additives to the concrete reduced the carbonate leaching. Acidic CO/sub 2/-containing waters were found to greatly increase carbonate leaching from concrete. Sea water was found to leach less carbon from carbonate concretes than either distilled water or Columbia River water, which showed nearly equivalent leaching. Basedmore » on our work, calcium, barium, and strontium carbonates in concrete are the most suitable waste forms for carbon-14, with calcium carbonate concrete slightly superior to the others. If the waste form is to be exposed to natural waters, sea water will have the lowest leach rate. 6 figures, 7 tables.« less