Statistical overview of findings by IR-inspections of PV-plants

First statistical evaluation of IR-inspections of PV-plants reveals that 86% of the installed PV-plants show IR-abnormalities. More than 120 PV-plants with more than 160,000 PV-modules were inspected and evaluated statistically. Main IR-abnormalities or failures in modules and string installations are analyzed, respectively. The average failure rate for PV-modules is about 8% and for module strings approximately 4%. The differentiation between the installation locations reveals that small residential installation show relatively more defective modules than large field installations. – Therefore, IR-imaging is a valuable method to give fast and reliable information about the actual quality and failure rate in inspected PV-installations.

[1]  Dirk Jordan,et al.  Compendium of photovoltaic degradation rates , 2016 .

[2]  Christian Camus,et al.  Correlation between the generated string powers of a photovoltaic: Power plant and module defects detected by aerial thermography , 2016, 2016 IEEE 43rd Photovoltaic Specialists Conference (PVSC).

[3]  Gabi Friesen,et al.  Review of Failures of Photovoltaic Modules , 2014 .

[4]  Christian Camus,et al.  IR-images of PV-modules with potential induced degradation (PID) correlated to monitored string power output , 2016, Optics + Photonics for Sustainable Energy.

[5]  Christoph J. Brabec,et al.  Reliability of IR-imaging of PV-plants under operating conditions , 2012 .

[6]  C. Buerhop-Lutz,et al.  The Role of Infrared Emissivity of Glass on IR-Imaging of PV-Plants , 2011 .

[7]  Christian Camus,et al.  aIR-PV-Check of Thin-Film PV-Plants – Detection of PID and Other Defects in CIGS Modules , 2016 .

[8]  Christian Camus,et al.  aIR-PV-check: A quality inspection of PV-power plants without operation interruption , 2016, 2016 IEEE 43rd Photovoltaic Specialists Conference (PVSC).

[9]  Degradation rate evaluation of multiple PV technologies from 59,000 modules representing 252,000 modules in four climatic regions of the United States , 2016, 2016 IEEE 43rd Photovoltaic Specialists Conference (PVSC).

[10]  Dirk C. Jordan,et al.  Photovoltaic Degradation Rates—an Analytical Review , 2012 .

[11]  Michael G. Deceglie,et al.  PV degradation methodology comparison — A basis for a standard , 2016, 2016 IEEE 43rd Photovoltaic Specialists Conference (PVSC).

[12]  P. Lechner,et al.  PID-Behaviour of Thin-Film- and c-Si PV-Modules , 2013 .

[13]  C. Buerhop-Lutz,et al.  Inspecting PV-plants using aerial, drone-mounted infrared thermography system , 2015 .