Effect of hole lubrication on the fretting fatigue life of double shear lap joints: An experimental and numerical study

Abstract In this research the affect that lubrication at a hole and pin connection has on the fatigue life of a double shear lap joint is studied both experimentally and numerically. The study focuses on the joint middle plate item, which is connected via a central hole to the outer plates by means of a clearance fitting pin, thereby placing the hole in double shear. In the experimental work three identical batches of fatigue specimens, which are made from aluminum alloy 2024-T3, were fatigue tested. In the first batch the surface of the fastener hole was not lubricated whilst the hole in the other two batches was lubricated – each batch using a different lubricant. The three batches of double shear lap joint specimens were fatigue tested and their S – N curves established. The results show that the specimens in which the holes were lubricated have better fatigue lives than the non-lubricated hole specimens. In the numerical study, FE simulations were performed to include hole lubrication effect on the stress distribution by using different friction coefficient at the interface of the hole and its fastener (pin). The FE results have helped to gain an understanding of the reasons for fatigue life improvement and also have helped to quantify the level of improvement.

[1]  Jeffrey Vogwell,et al.  A novel method of cold expansion which creates near‐uniform compressive tangential residual stress around a fastener hole , 2004 .

[2]  S. Adibnazari,et al.  A simple relation in elastic contact problems , 2008 .

[3]  S. Mall,et al.  Wear characterization of Ti–6Al–4V under fretting–reciprocating sliding conditions , 2008 .

[4]  David Taylor,et al.  On the prediction of high-cycle fretting fatigue strength: Theory of critical distances vs. hot-spot approach , 2008 .

[5]  Krishnakumar Shankar,et al.  Fatigue behaviour of aluminium alloy 7075 bolted joints treated with oily film corrosion compounds , 2002 .

[6]  Jeffrey Vogwell,et al.  The effect of bolt clamping force on the fracture strength and the stress intensity factor of a plate containing a fastener hole with edge cracks , 2009 .

[7]  D. A. Hills,et al.  Recent developments in the understanding of fretting fatigue , 2013 .

[8]  C. Navarro,et al.  On the use of multiaxial fatigue criteria for fretting fatigue life assessment , 2008 .

[9]  S. Sapuan,et al.  Fretting fatigue crack initiation: An experimental and theoretical study , 2007 .

[10]  S. Leen,et al.  A combined wear and crack nucleation–propagation methodology for fretting fatigue prediction , 2008 .

[11]  Farshid Sadeghi,et al.  Fretting fatigue of rough surfaces , 2008 .

[12]  Jeffrey Vogwell,et al.  Experimental and numerical investigations into the effect of an interference fit on the fatigue life of double shear lap joints , 2009 .

[13]  S. Raman,et al.  Effect of contact pressure on fretting fatigue behaviour of Al–Mg–Si alloy AA6061 , 2005 .

[14]  Jeffrey Vogwell,et al.  The effect of cold expansion on improving the fatigue life of fastener holes , 2003 .

[15]  S. Raman,et al.  Effect of shot blasting on plain fatigue and fretting fatigue behaviour of Al–Mg–Si alloy AA6061 , 2005 .

[16]  A finite element analysis of fretting fatigue crack growth behavior in Ti–6Al–4V , 2008 .

[17]  Jeffrey Vogwell,et al.  Effect of torque tightening on the fatigue strength of bolted joints , 2006 .

[18]  D. Hills,et al.  Prediction of fretting crack propagation based on a short crack methodology , 2008 .

[19]  Patrick J. Golden,et al.  A fracture mechanics life prediction methodology applied to dovetail fretting , 2006 .

[20]  Jeffrey Vogwell,et al.  Experimental and numerical investigation of the effect of clamping force on the fatigue behaviour of bolted plates , 2008 .

[21]  T. N. Chakherlou,et al.  An experimental investigation on the effect of short time exposure to elevated temperature on fatigue life of cold expanded fastener holes , 2008 .

[22]  Mechanics of two-stage crack growth in fretting fatigue , 2008 .