InAs Quantum Dots in AlAs/GaAs Short Period Superlattices: Structure, Optical Characteristics and Laser Diodes

Abstract : The influence of two monolayer - thick AlAs under- and overlayers on the formation and properties of self-assembled InAs quantum dots (QDs) has been studied using transmission electron microscopy (TEM) and photoluminescence (PL). Single sheets of InAs QDs were grown inside a 2 ML/8 ML AlAs/GaAs short-period superlattice with various combinations of under- and overlayers. It was found that 2.4 ML InAs QDs with GaAs underlayer and 2 ML AlAs overlayer exhibited the lowest QD surface density of 4.2 x 10(exp 10)/sq cm and the largest QD lateral size of about 19 nm as compared to the other combinations of cladding layers. This InAs QD ensemble has also shown the highest room temperature PL intensity with a peak at 1210 mn and the narrowest linewidth, 34 meV. Fabricated edge-emitting lasers using triple layers of InAs QDs with AlAs overlayer demonstrated 120 A/sq cm threshold current density and 1230 nm emission wavelength at room temperature. Excited state QD lasers have shown high thermal stability of threshold current up to 130 deg C.

[1]  G. Abstreiter,et al.  Influence of a thin AlAs cap layer on optical properties of self-assembled InAs/GaAs quantum dots , 1999 .

[2]  O. Brandt,et al.  Effect of In segregation on the structural and optical properties of ultrathin InAs films in GaAs , 1992 .

[3]  P. G. Piva,et al.  Manipulating the energy levels of semiconductor quantum dots , 1999 .

[4]  A. Stintz,et al.  Very low threshold current density room temperature continuous-wave lasing from a single-layer InAs quantum-dot laser , 2000, IEEE Photonics Technology Letters.

[5]  B. A. Joyce,et al.  Composition of InAs quantum dots on GaAs(001): Direct evidence for (In,Ga)As alloying , 1998 .

[6]  Gerhard Abstreiter,et al.  Influence of growth conditions on the photoluminescence of self-assembled InAs/GaAs quantum dots , 1999 .

[7]  Andreas Stintz,et al.  Transition dipole moment of InAs/InGaAs quantum dots from experiments on ultralow-threshold laser diodes , 2000 .

[8]  J. Merz,et al.  Volmer–Weber and Stranski–Krastanov InAs-(Al,Ga)As quantum dots emitting at 1.3 μm , 2000 .

[9]  S. Denbaars,et al.  Direct formation of quantum‐sized dots from uniform coherent islands of InGaAs on GaAs surfaces , 1993 .

[10]  G. Park,et al.  Temperature dependence of lasing characteristics for long-wavelength (1.3-μm) GaAs-based quantum-dot lasers , 1999, IEEE Photonics Technology Letters.

[11]  J. Lott,et al.  Application of self-organized quantum dots to edge emitting and vertical cavity lasers , 1998 .

[12]  H. Sakaki,et al.  Multidimensional quantum well laser and temperature dependence of its threshold current , 1982 .